导电聚苯胺性能优异,应用前景广阔.采用原位聚合法在不锈钢表面制备了绿色导电聚苯胺(Pan)薄膜,研究了苯胺(An)与硫酸的物质的量浓度比、苯胺(An)与过硫酸铵(APS)的物质的量浓度比以及反应温度对合成的影响.用点滴试验、阳极极化曲线评价了聚苯胺薄膜的耐腐蚀性能.通过正交试验确定了本试验条件下的最优工艺条件为:c(An):c(H2SO4)=1:3,c(An):c(APS)=1:1,反应温度为18℃;通过阳极极化曲线测试发现,在最优工艺条件下制备的覆盖了聚苯胺薄膜的不锈钢试片在3.5%NaCl溶液中点腐蚀电位正移了1 000 mV左右.说明该聚苯胺薄膜具有较好的耐腐蚀性能.
参考文献
| [1] | DeBerry D W .Modification of the electrochemical and corrosion behavior of stainless steels an electroactive coating[J].Journal of the Electrochemical Society,1985,132(05):1 022-1 026. |
| [2] | Schoch KF.;Buckley LJ.;Byers WA. .DEPOSITION AND CHARACTERIZATION OF CONDUCTING POLYMER THIN FILMS ON INSULATING SUBSTRATES[J].Synthetic Metals,1995(1):13-23. |
| [3] | Avlyanov JK.;Macdiarmid AG.;Josefowicz JY. .ATOMIC FORCE MICROSCOPY SURFACE MORPHOLOGY STUDIES OF IN SITU DEPOSITED POLYANILINE THIN FILMS[J].Synthetic Metals,1995(3):205-208. |
| [4] | J. Stejskal;I. Sapurina .In-situ polymerized polyaniline films[J].Synthetic Metals,1999(3):195-202. |
| [5] | Andrea R;Martin H;Irina S.In Situ Polymerizod Polyaniline Films[J].Journal of Colloid and Interface Science,2002(48):413-418. |
| [6] | 潘玮,黄素萍,龚静华.聚苯胺/涤纶导电纤维的制备及其织物抗静电性能研究[J].合成纤维,2002(01):30-32. |
| [7] | 邓建国,贺传兰,王建华.浸渍吸附聚合法合成聚氨酯/聚苯胺抗静电材料[J].工程塑料应用,2004(11):28-31. |
| [8] | 陶雪钰,陈骁,熊忠,李鹏,吴其晔.原位聚合沉积透明导电聚苯胺薄膜的研究进展[J].化学推进剂与高分子材料,2005(06):23-26. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%