采用电渗析法研究了化学镀镍废液的再生工艺,分析了温度、膜间距以及物料流速对镀液中HPO32-的去除率以及Ni2+、H2PO2-损失率的影响.得出适宜的工艺条件为:温度26℃,膜间距5 cm,物料流速25 s/L.对再生镀液所得镀层的性能进行了测试,并通过扫描电镜和X射线衍射进行了微观形貌及结构分析.结果表明:在适宜条件下再生镀液所得镀层的性能与新开缸镀液所得镀层相近,其微观形貌与新开缸镀液使用至第三周期所得镀层的微观形貌相似,该镀层具有非晶态结构.
参考文献
| [1] | CROOPNICK G A;SCRUGGS D M;DONALDSON J .A low environmental-risk replacement for chromium and electroless nickel[J].Metal Finishing,1994,92(04):13-16. |
| [2] | R. N. Duncan .The Metallurgical Structure of Electroless Nickel Deposits: Effect on Coating Properties[J].Plating & Surface Finishing,1996(11):65-69. |
| [3] | Li C.L.;Tsuru T.;Zhou D.;Matsumura M.;Zhao H.X. .Recovery of spent electroless nickel plating bath by electrodialysis[J].Journal of Membrane Science,1999(2):241-249. |
| [4] | Paul T. Bolger;David C. Szlag .Investigation into the rejuvenation of spent electroless nickel baths by electrodialysis[J].Environmental Science & Technology: ES&T,2002(10):2273-2278. |
| [5] | 王昊,刘贵昌,邢明秀,王立达.电解法降解化学镀镍废液COD的研究[J].环境保护与循环经济,2011(05):47-49,75. |
| [6] | 赵立新,印博林,张宁,姜海涛,邵忠财.自催化还原法回收化学镀镍废液[J].电镀与精饰,2012(04):26-29. |
| [7] | 王玮 .综合法再生化学镀镍老化液的研究[D].大连:大连理工大学,2010. |
| [8] | CROTTY D E;BAILEY D E .Electrodialysis of electroless nickel process solutions:Continuous versus batch treatment designs[J].Metal Finishing,2002,100(11/12):30-31,33-39. |
| [9] | Peter D.Longfield;Rick Rauppius;Werner Richtering .Novel Long-Life Electroless Nickel with Continuous Regeneration by Electrodialysis[J].Metal finishing,2001(5):36,38-43-0. |
| [10] | 李朝林;周定;唐彩红 .电渗析法再生化学镀镍液的研究[J].电镀与环保,1997,17(01):13-15. |
| [11] | 何湘柱,宋清,赵国鹏.电渗析法再生化学镀镍废液膜的选择及电流和时间的影响[J].电镀与涂饰,2012(09):33-36. |
| [12] | 赵雨 .化学镀镍废液再生的电渗析法研究[D].广东工业大学,2011. |
| [13] | 宫成云 .电化学与化学法结合再生化学镀镍老化液[D].大连理工大学,2009. |
| [14] | 殷雪峰 .用电渗析法净化化学镀镍老化液之研究[D].大连理工大学,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%