采用60tBOF→60tLF→200mm×200mm方坯CC工艺生产Cf53钢,冶炼与连铸工艺要点包括：控制转炉终点成分、温度和下渣量;控制LF炉渣碱度R在4.0～5.5之间,渣中w（Al2O3）15%～20%、w（MnO＋FeO）〈1.5%;优化喂线工艺,保证白渣保持时间不小于15min;采用全保护浇铸和M＋F电磁搅拌等。检验结果表明,采用该工艺生产的Cf53钢中,w（O）平均为6.6×10-6,w（N）平均为73.55×10-6,铸坯缩孔和中心疏松均在1.0级以下,明显改善了铸坯的宏观组织形貌。
Cf53 steel is produced at Jiyuan Steel by using 60tBOF-60t LF 200 mm× 200 mm CC processes. The key smelting and casting technologies are as follows, controlling of BOF endpoint compositions, temperature and the quantity of slag controlling of slag basicity R for LF in a range of 4-5.5, Al2O3 content in slag 15 %-20 %, w（MnO＋ FeO） 〈1.5 %, optimizing of wire feeding process to ensure white slag retaining time not less than 15 minutes adopting of whole protective casting and M-kF electromagnetic stirring. Testing results showed that Cf53 steel produced by the technologies has good quality and properties, average [O] 6.6 ×10-6, average [N] 73.55 ×10-6, casting shrinkage and porosity are in Rank 1, which means the macro morphology of casting billet are significantly improved.
参考文献
| [1] | 谢文新,惠荣.连铸工艺开发SAE1141汽车用易切削钢[J].钢铁,2004(12):29-32. |
| [2] | 张雪松.改善碳素结构钢钢水流动性的研究[J].江苏冶金,1998(03):3-5. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%