Slag Melting Characteristic of Slag Forming and Slag Splashing for BOF Less Slag Smelting

钢铁研究学报(英文版), 2012, 19(7): 20-32.

Slag Melting Characteristic of Slag Forming and Slag Splashing for BOF Less Slag Smelting

^1, , ^2, , ^3, , ^4, , ^5, , ^6,

1.Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China

2.Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China

3.Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China

4.Steelmaking Works, Shougang Jingtang Iron and Steel Co Ltd, Tangshan 063200, Hebei, China

5.Steelmaking Works, Shougang Jingtang Iron and Steel Co Ltd, Tangshan 063200, Hebei, China

6.Steelmaking Works, Shougang Jingtang Iron and Steel Co Ltd, Tangshan 063200, Hebei, China

基金项目: Item Sponsored by National Science and Technology Support Program for llth Five-Year Plan of China (2006BAE03A00)

关键词：少渣冶炼 , 炉渣碱度 , 溅渣护炉 , 熔融特性 , 造渣 , 转炉 , 化学组合物 , 熔点测定

Slag Melting Characteristic of Slag Forming and Slag Splashing for BOF Less Slag Smelting

WU Wei ^1, , MENG Hua-dong ^2, , LIU Liu ^3, , YUAN Tian-xiang ^4, , BAI Yan-jiang ^5, , YAN Zhan-hui ^6,

1.Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China

2.Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China

3.Metallurgical Technology Research Department, Central Iron and Steel Research Institute, Beijing 100081, China

4.Steelmaking Works, Shougang Jingtang Iron and Steel Co Ltd, Tangshan 063200, Hebei, China

5.Steelmaking Works, Shougang Jingtang Iron and Steel Co Ltd, Tangshan 063200, Hebei, China

6.Steelmaking Works, Shougang Jingtang Iron and Steel Co Ltd, Tangshan 063200, Hebei, China

Keywords： less slag smelting , melting point determination , petrographic analysis , slag forming process slag splashing ,

The slag melting characteristic of slag forming and slag splashing for 300 t BOF less slag process is researched by combining the methods of the slag chemical composition, the melting point determination and the petrographic analysis. The results show that the melting point of final slag for less slag smelting is 20 ~C lower than that for conventional smelting. According to results of the petrographic analysis, the C3S （3CaO ~ SiO2） and C2S （2CaO · SiO2） content for less slag smelting are lower than those for conventional smelting, while the RO （FeO, MgO, MnO, etc） phase and C4AF （4CaO · Al2O3· Fe2O3） phase are higher than those for conventional smelting. According to results of the chemical analysis, the （CaO） content and slag basicity for less slag smelting are higher than those for conventional smelting, while （FeO） and （MgO） content in slag for less slag smelting are almost equal to those for conventional smelting. The reason why slag melting point for less slag smelting is lower than that for con- ventional smelting is that the quantity of added fluorite for less slag smelting is more than that for conventional smel- ting. According tO the analysis results the slag melting point is determined by the C3S, C2S, RO phase and C4AF content. According to the results of slag melting characteristic before and after slag splashing for less slag smelting, the present adjusting slag process has little effect. It is important to adjust the composition of BOF final slag. The （FeO） content in slag is to be reduced at the slag splashing and adjusting slag process for less slag smelting.

参考文献

[1]	JIANG Xiao fang;CHEN Zhao ping .Practice of Less Slag Steelmaking at Baosteel[J].Baosteei Technology,2003,21(01):6.
[2]	YIN Rui-yu .Development of Steelmaking and Continuous Casting Technology and Prospect oi This Technology in 2010 in China[J].Steelmaking,2008,24(06):1.
[3]	刘浏.如何建立高效低成本洁净钢平台[J].钢铁,2010(01):1-9.
[4]	赵素华,潘秀兰,梁慧智.少渣炼钢工艺的进步与展望[J].鞍钢技术,2008(06):13-16,24.
[5]	孟华栋,刘浏.转炉炼钢成渣过程的岩相研究[J].钢铁,2010(06):26-30.
[6]	杨文远,王明林,崔淑贤,干勇.炉渣的岩相研究在转炉炼钢中的应用[J].钢铁研究学报,2007(12):10-15.
[7]	沙骏,朱苗勇,万利成,郭宝志.转炉溅渣护炉炉渣物性研究[J].炼钢,2001(04):36-39.
[8]	BAI Rui-guo;ZHANG Xing-li;QIAO Hai-lin .Research About Slag-Splashing Furnace-Protecting Technology for 20 t Oxygen Top-Blown Converter in Chengde Iron and Steel Com- pany[J].Hebei Metallurgy,2000,116(02):45.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Slag Melting Characteristic of Slag Forming and Slag Splashing for BOF Less Slag Smelting

Slag Melting Characteristic of Slag Forming and Slag Splashing for BOF Less Slag Smelting

参考文献