论述了非均相沉淀法制备纳米α—Al2O3/W复合粉体的实验过程,以及纳米钨粉对α—Al2O3相转变温度的影响.结果表明:纳米钨粉的存在降低了α—Al2O3的相转变温度.本实验所制凝胶在1000℃真空中煅烧1h可获得平均粒径<50nm的α—Al2O3/W粉体.
Al2O3/5vol%W and Al2O3/10vol%W nanocomposite powders, with mean particle size less than 50nm, were prepared by the heterogeneous precipitation
process using Al(NO3)3·9H2O and (NH4)2CO3 solutions as raw materials and tungsten nanometer powders as additives in different ratios. α-Al2O3/W
nanocomposite was obtained by calcining Al(OH)3/W dried gel at 1000℃ for 1h in vacuum. Adding tungsten nanometer powders can reduce the phase transformation
temperature to alpha alumina. The composite powder is simply mechanically mixed together, alumina coating is on the surfaces of nanometer tungsten powder.
参考文献
| [1] | 孙旭东, 李继东, 张民, 等．金属学报, 1999, 35 (8): 879--882. [2] 吕珺, 郑志群, 金志浩． 复合材料学报, 2001, 18 (4): 76--81. [3] 王宏志, 高濂, 归林华, 等(WANG Hong-Zhi, et al)． 无机材料学报 (Journal of Inorganic Materials), 1999, 14 (2): 280--286. [4] Srdic V V, Winterer M, Miehe G, et al. NanoStructured Mater., 1999, 12: 95--100. [5] Zhu W Z, Gao J H, Ding Z S. J. Mater. Sci. Lett., 1997, 32: 537--542. [6] Xu B S, Tanaka S I. Supramolecular Sci., 1998, 5: 227--228. [7] 刘政, 刘小梅, 朱应禄, 等． 矿冶, 1999, 8 (3): 65--69. [8] 李海林, 邬~~柱, 王正东, 等 (LI Hai-Lin, et al)．无机材料学报 (Journal of Inorganic Materials), 1995, 10 (3): 313--317. [9] Naser J, Ferkel H. NanoStructured Mater., 1999, 12: 451--454. [10] Bhattacharya P, Chattopadhyay k. NanoStructured Mater., 1999, 12: 1077--1080. [11] 李国军, 赵世柯, 黄校先, 等 (LI Guo-Jun, et al)．无机材料学报 (Journal of Inorganic Materials), 2002, 17 (2): 235--240. [12] 卢金山, 高濂, 归林华, 等 (LU Jin-Shan, et al)．无机材料学报(Journal of Inorganic Materials), 2001, 16 (2): 277--282. [13] 张金咏, 傅正义, 王为民．武汉工业大学学报, 1999, 21 (2): 10--13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%