Superplasticity in intermetallic alloys is reviewed. Intermetallics which have been demonstrated to be superplastic include nickel-based (Ni_3Al, Ni_3Si), titanium-base (Ti_3Al, TiAl), and iron-base (Fe_3Al, FeAl) alloys. These alloys are primarily finegrained, two phase materials. But, superplasticity was also observed in some iron-base alloys which were in coarsegrained conditions. These alloys behave like Class I solid solution. The superplastic deformation mechanisms as well as microstructural characteristics are discussed. The superplastic forming of intermetallics is also briefly addressed.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] | |
| [15] | |
| [16] | |
| [17] | |
| [18] | |
| [19] | |
| [20] | |
| [21] | |
| [22] | |
| [23] | |
| [24] | |
| [25] | |
| [26] | |
| [27] | |
| [28] | |
| [29] | |
| [30] | |
| [31] | |
| [32] | |
| [33] | |
| [34] | ．KochC．C．,StoloffN．S．,andLiuC．T．,ed．High-TemperatureOrderedIntermetallicAlloys．Vol．39,MaterialsResearchSociety,Pittsburgh,PA(1985)．2．StoloffN．S．,KochC．C．,LiuC．T．,andIzumiO,ed．HighTemperatureOrderedIntermetallicAlloysII,MRSSym．vol．81．MaterialsResearchSociety,Pittsburgh,PA(1987)．3．LiuC．T．,TaubA．I．,StoloffN．S．,andKochC．C．,ed．HighTemperatureOrderedIntermetallicAlloysIII,MRSSym．vol．133．MaterialsResearchSociety,Pittsburgh,PA(1989)．4．JohnsonL．A．,PopeD．,andStieglerJ．,ed．HighTemperatureOrderedIntermetallicAlloysIV,MRSSym．vol．213．MaterialsResearchSociety,Pittsburgh,PA(1991)．5．BakerI．,DaroliaR．,WhittenbergerJ．D．,andYooM．H．,ed．HighTemperatureOrderedIntermetallicAlloysV,MRSSym．Vol．288．MaterialsResearchSociety,Pittsburgh,PA(1993)．6．HanadaS．,SatoT．,WatanabeS．,andIzumiO．,J．JpnInst．Metals,1981 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%