The directional solidification has been carried out for the Al-4Bi-2.5Co (wt pct) alloys with different melt superheat temperatures. The microstructure characterization and the quantitative metallographic analysis have been performed. The results indicated that the Bi-rich sphere size and cellular spacing decrease with increasing melt superheat temperature. The interaction between the advancing solidification interface and the Bi-rich spheres with different sizes was analyzed. The effect of the melt superheat treatment on microstructure evolution was discussed for the immiscible alloys. The microstructure development in ternary Al-Bi-Co alloys directionally solidified with different melt superheat temperatures was clarified.
参考文献
| [1] | L.J.Hayes;J.B.Andrews .Effect of convective instability in directionally solidified hypermonotectic Al-In alloys[J].Materials Science Forum,2000(0):209-218. |
| [2] | Q.D. Qin;Y.G. Zhao;Y.H. Liang .Effects of melt superheating treatment on microstructure of Mg_2Si/Al-Si-Cu composite[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):106-109. |
| [3] | F.S. Yin;X.F. Sun;H.R. Guan .Effect of thermal history on the liquid structure of a cast nickel-base superalloy M963[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2004(1/2):225-228. |
| [4] | M.M. Haque;Ahmad F. Ismail .Effect of superheating temperatures on microstructure and properties of strontium modified aluminium-silicon eutectic alloy[J].Journal of Materials Processing Technology,2005(0):312-316. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%