Superplasticity Enhanced by Two-stage Deformation in a Hot-extruded AZ61 Magnesium Alloy

材料科学技术（英文）, 2005, 21(1): 71-74.

^1, , ^2,

1.Department of Materials Engineering, Dalian University of Technology, Dalian 116024, China

2.Institute of Materials Science and Engineering, National Sun Yat-San University, Kaohsiung 804, Taiwan, China

Superplasticity Enhanced by Two-stage Deformation in a Hot-extruded AZ61 Magnesium Alloy

A two-stage strain rate deformation method is proposed to enhance the superplasticity in a hot extruded AZ61alloy. In the stage-one of deformation, a relatively high strain rate was applied in order to obtain fine grains through dynamic recrystallization. The optimum strain rate for DRX at 300℃ was identified as ～5×10-3 s-1. Stage-two is conducted at relatively low strain rate in order to utilize the fine grains refined by DRX during stage-one to make the grain boundary sliding operate more smoothly, which resulting in enhanced superplastic elongation from 350%to 440%.

参考文献

[1]	Y.N. Wang;J.C. Huang .Comparison of grain boundary sliding in fine grained Mg and Al alloys during superplastic deformation[J].Scripta materialia,2003(8):1117-1122.
[2]	HWatamae;TMukai;KHigashi .[J].Scripta Materialia,1999,40:477.
[3]	MMauchi;KAmeyama;HIwasaki;KHigashi .[J].Acta Materialia,1999,47:2047.
[4]	HWatamae;TMukai;MKohzu .[J].KHigashi:Acta Mater,1999,47:3753.
[5]	ZHorita;KMataubara;KMakii;TGLangdon .[J].Scripta Materialia,2002,47:255.
[6]	Aussia;ABArtzy;AShtechman .[J].Materials Science and Engineering,2001,302:A56.
[7]	H. K. Lin;J. C. Huang .High strain rate and/or low temperature superplasticity in AZ31 Mg alloys processed by simple high-ratio extrusion methods[J].Materials transactions,2002(10):2424-2432.
[8]	H.K. Lin;J.C. Huang .Fabrication of Low Temperature Superplastic AZ91 Mg Alloys Using Simple High-Ratio Extrusion Method[J].Key engineering materials,2003(2):875-880.
[9]	HTakuda;SKikuchi;NHatta .[J].Journal of Materials Science,1992,27:937.
[10]	TMohri;MMabuchi;MNakamura;TAsahiha HIwasaki TAizawa KHigashi .[J].Materials Science and Engineering,2000,290:A139.
[11]	XWu;YLiu .[J].Scripta Materialia,2002,46:269.
[12]	J. C. Tan;M. J. Tan .Superplasticity in a rolled Mg-3Al-1Zn alloy by two-stage deformation method[J].Scripta materialia,2002(2):101-106.
[13]	JCTan;MJTan .[J].Materials Science and Engineering,2003,339:A81.
[14]	JCTan;MJTan .[J].Materials Science and Engineering,2003,339:A124.
[15]	ODShery;JWadsworth .[J].Journal of Progress in Materials Science,1989,33:169.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Superplasticity Enhanced by Two-stage Deformation in a Hot-extruded AZ61 Magnesium Alloy

参考文献