采用声发射技术研究了304不锈钢在0.01和0.05 mol·L-NaCl溶液中的腐蚀过程,应用光学显微镜观察了腐蚀前后试样表面形貌.结果表明,0.01和0.05 mol·L-浓度下,304不锈钢腐蚀产生的声发射起始幅度不同,随时间延长,声发射幅度阶跃,直至达到最终的稳定幅度,这说明随浸泡时间延长,试样腐蚀程度加深.浸泡初期,声发射相对能量较高,声发射相对能量随浸泡时间延长而降低,但仍具有比较明显的相对能量积聚区,0.05 mol·L-1浓度时更为明显,同时其振铃数聚类区多于0.01 mol·L-1.浸泡4h后,试样表面发生了晶间腐蚀和点蚀.相比0.01 mol·L-1浓度,0.05 mol·L-下试样表面点蚀数量增多、点蚀孔尺寸增大.
参考文献
| [1] | 孙鹏飞,张来启,林均品.304不锈钢/Ti-45Al-8Nb电火花沉积涂层在熔锌中的腐蚀行为[J].材料热处理学报,2014(02):151-156. |
| [2] | Jian Xu;Xinqiang Wu;En-Hou Han .Acoustic emission response of sensitized 304 stainless steel during intergranular corrosion and stress corrosion cracking[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013(Aug.):262-273. |
| [3] | G. Du;J. Li;W.K. Wang;C. Jiang;S.Z. Song .Detection and characterization of stress-corrosion cracking on 304 stainless steel by electrochemical noise and acoustic emission techniques[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(9):2918-2926. |
| [4] | M. Mohammad;S. Abdullah;Jamaludin;O. Innayatullah .Predicting the fatigue life of the SAE 1045 steel using an empirical Weibull-based model associated to acoustic emission parameters[J].Materials & design,2014(Feb.):1039-1048. |
| [5] | 杜刚,梁君,冯忠伟,李金龙.基于声发射技术304不锈钢极化条件耐蚀性能研究[J].计算机测量与控制,2013(10):2770-2772,2779. |
| [6] | 龚利华,张波,江琳琳.不锈钢作为给水材料在含Cl-水中的腐蚀行为[J].腐蚀与防护,2007(08):400-402. |
| [7] | 杨瑞成,毕海娟,牛绍蕊,靳塞特,申鹏.温度和Cl-质量分数对304不锈钢耐点蚀性能的影响[J].兰州理工大学学报,2010(05):5-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%