利用可变速率比高能行星球磨机的不同转速及球磨时间,通过干湿球磨法成功制备了均匀的石墨烯.分别使用X射线粉末衍射仪(XRD)、扫描电子显微镜(SEM),拉曼光谱仪以及透射电子显微镜(TEM)对其进行结构表征和分析.并将该石墨烯作为摩擦性能添加剂添加到基础油中,使用UMT-2型摩擦磨损试验机对其摩擦学性能进行测试,实验结果表明石墨烯作为添加剂具有良好的减摩抗磨性能.
参考文献
| [1] | Novoselov K S;Geim A K;Morozov S V et al.Electric Feld Efect in Atomically Thin Carbon Fills[J].SCIENCE,2004,306:666-669. |
| [2] | Kroto H W;Hcath J R;OBrien SC;Curl RF .C60:Buckminsterfullerene[J].NATURE,1985,318:162-163. |
| [3] | Iijima S .Helical mierotubules of graphitic carbon[J].NATURE,1991,354:56-58. |
| [4] | Balandin AA;Ghosh S;Bao WZ;Calizo I;Teweldebrhan D;Miao F;Lau CN .Superior thermal conductivity of single-layer graphene[J].Nano letters,2008(3):902-907. |
| [5] | Changgu Lee;Xiaoding Wei;Jeffrey W. Kysar;James Hone .Measurement of the Elastic Properties and Intrinsic Strength of Monolayer Graphene[J].Science,2008(5887):385-388. |
| [6] | Chert J H;Jang C;XiaoS D .Effciency of the CNT/graphene/nSi ternary heter-ojunction solar[J].Nature Nanotechnology,2008,3:206-209. |
| [7] | Zhang Y;Tan J W;Kim P et al.Experimental observationof the quantum Hall effect and Berry ～ phase in graphene[J].NATURE,2005,438:201-204. |
| [8] | Obraztsov, AN .CHEMICAL VAPOUR DEPOSITION Making graphene on a large scale[J].Nature nanotechnology,2009(4):212-213. |
| [9] | Tung, VC;Allen, MJ;Yang, Y;Kaner, RB .High-throughput solution processing of large-scale graphene[J].Nature nanotechnology,2009(1):25-29. |
| [10] | 张泰然,孙陆威,何海平,叶志镇.化学法制备水溶性良好的石墨烯及其荧光淬灭应用[J].材料科学与工程学报,2013(04):484-488. |
| [11] | Dan Li;Richard B. Kaner .Graphene-Based Materials[J].Science,2008(5880):1170-1171. |
| [12] | Ferrari AC;Meyer JC;Scardaci V;Casiraghi C;Lazzeri M;Mauri F;Piscanec S;Jiang D;Novoselov KS;Roth S .Raman spectrum of graphene and graphene layers[J].Physical review letters,2006(18):7401-1-7401-4-0. |
| [13] | Tomimoto M;Mizuhara K;Yamamot T .Effect of particles on lubricated friction-Verification of dead time phenomenon and friction theory[J].Tribology Transactions,2002,45(01):94-102. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%