利用界面聚合技术制备了以聚脲为壁材的热显影微胶囊。采用热重-差示扫描量热分析技术（TG／DSC）研究了聚脲囊壁的热稳定特性；利用红外光谱技术对显色剂D-8在不同温度及时间条件下热渗透结果进行了检测，并与微胶囊显影密度随加热时间及温度的变化进行了对比。实验结果表明，由IPDI聚合形成的聚脲囊壁热稳定温度在250℃左右，在170℃附近发生玻璃态到高弹态的相转变；显色剂D8的渗透率随加热温度升高呈单指数增长而随加热时间的延长呈线性增长；微胶囊显影密度随加热温度及时间的增加而增大，且热显影结果与红外检测结果具有较好的一致性。
The thermal development microcapsule with polyurea shell was synthesized with interracial polymeri- zation method, which was a type of information display material. Thermal properties of polyurea shell are stud- ied by TG/DSC thermal analysis technology. The permeation of developer D-8 was realized by heating method at different temperature and times. The permeation results are detected by infrared spectroscopy technology, and compared with the changes of image density of sample versus the temperature and heating time. The results show that thermal stability temperature of microcapsule shell synthesized by isophorone diisocyanate （IPDI） was about 250℃, and the phase change temperature Tg was about 170℃. The results of infrared spectroscopy show that permeability of developer 13-8 increases exponentially with the heating temperature, but increases lin- early with the heating time. Image density of sample increases gradually with temperature and heating time, and there are good consistency between the results of thermal development and the result of infrared spectroscopy.
参考文献
| [1] | 魏杰,李刚强,王潇,管卫文.微胶囊成像材料应用进展[J].信息记录材料,2008(02):31-36. |
| [2] | BA Xinwu,AN Puying,LU Shuang,LIU Guangtian.Preparation and Characterization of Heat Sensitive Color-developing Microcapsules[J].中国化学(英文版),2009(06):1153-1158. |
| [3] | K.Sawada;H.Urakawa .Preparation of photosensitive color-producing microcapsules utilizing in situ polymerization method[J].Dyes and Pigments,2005(1):45-49. |
| [4] | 荣宇,吴刚,陈红征,汪茫.电子墨水微胶囊及电泳显示原型器件的制备[J].高等学校化学学报,2005(05):982-984. |
| [5] | Li Xiaowei;Jiang Xiaoli;Lai Weidong et al.Investiga-tion of a light-thermal sensitive imaging system based on the mierocapsule technique[J].Journal of Imaging Sci-ence and Technology,2007,51(02):122-126. |
| [6] | 左朝阳,王建平,王登武,赵晓鹏.明胶-阿拉伯树胶基电子墨水微胶囊的制备及其显示性能[J].功能材料,2006(09):1504-1506. |
| [7] | 刘艳芳,王星,葛丽芹,巴龙.利用原子力显微镜测量复合微胶囊静态弹性性质[J].电子显微学报,2008(02):117-121. |
| [8] | 曹根庭,王征科,胡巧玲,刘俊奇,王幽香.聚电解质微胶囊的制备及其包埋释放行为[J].材料研究学报,2009(02):165-170. |
| [9] | 任晓亮,王立新,任丽,苏峻峰.原位聚合法制备相变储热微胶囊[J].功能材料,2005(11):1722-1724,1727. |
| [10] | 陆少锋,邢建伟,张昭环,贾高鹏.界面聚合聚脲微胶囊相变材料的研制与性能[J].高分子材料科学与工程,2010(12):39-41,45. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%