采用拉伸、夏比冲击、落锤撕裂(DWTT)及SEM等试验方法,研究了临界区热处理工艺生产的X80大变形管线钢微观组织和力学性能.研究结果表明:采用800～860℃保温15 min淬火后,强度可达到X80大变形管线钢要求,并具有优异的变形性能和极佳的低温冲击韧性,-20℃夏比冲击功均值大于240J,夏比冲击剪切面积均值大于90％,-15℃DWTT剪切面积均值大于85％,同时拉伸曲线呈拱顶型.上述工艺参数条件下淬火后,得到铁素体加马氏体双相组织,马氏体体积分数为16.1 ％～18.2％.
参考文献
| [1] | Furen Xiao;Bo Liao;Deliang Ren .Acicular ferritic microstructure of a low-carbon Mn-Mo-Nb microalloyed pipeline steel[J].Materials Characterization,2005(4/5):305-314. |
| [2] | Ming-Chun Zhao;Ke Yang;Yi-Yin Shan .Comparison on strength and toughness behaviors of microalloyed pipeline steels with acicular ferrite and ultrafine ferrite[J].Materials Letters,2003(9/10):1496-1500. |
| [3] | Zhenghua Tang;Waldo Stumpf .The effect of microstructure and processing variables on the yield to ultimate tensile strength ratio in a Nb-Ti and a Nb-Ti-Mo line pipe steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):391-402. |
| [4] | Hwang, B.;Lee, C.G. .Influence of thermomechanical processing and heat treatments on tensile and Charpy impact properties of B and Cu bearing high-strength low-alloy steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(16/17):4341-4346. |
| [5] | Y.Y.Hu;X.R.Zuo;R.T.Li et al.Effect of initial microstructures on the properties of ferrite-martensite dualphase pipeline steels with strain-based design[J].Materials Research,2012,15(02):317-322. |
| [6] | A.R.Marder .The Effect of Heat Treatment on the properties and structure of molybdenum and vanadium dualphase steels[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1981,12A:1569-1579. |
| [7] | M.Erdogan .Effect of austenite dispersion on phase transformation in dual phase steel[J].Scripta Materialia,2003,48(05):501-506. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%