针对丁腈橡胶（NBR）黏度过大和相转化时间较长难于纺制中空纤维的问题，采用先与聚氯乙烯（PVC）共混改性再用干-湿相转化的方法制备出轻质、低耗材的丁腈橡胶中空纤维阻尼新材料，探讨了NBR与PVC质量比和共混聚合物质量分数对NBR中空纤维阻尼及力学性能的影响。结果表明：中空纤维结构阻尼性能明显优于对应的平板膜结构；调整NBR与PVC质量比和共混聚合物质量分数可优化NBR中空纤维的拉伸性能及阻尼性能；可通过提高NBR与PVC质量比使NBR中空纤维阻尼材料的损耗因子峰值所对应的温度向低温方向偏移。共混聚合物质量分数为25％，NBR与PVC质量比为80：20时，NBR中空纤维阻尼损耗因子最大，达到0．78。
NBR （nitrile-butadiene rubber） hollow fibers have been prepared by the method of dry - wet phase inversion, in which PVC（polyvinylchloride） was blended to avoid the problems of NBR because of being too viscous and too long time of phase inversion. The NBR hollow fibers may be a new lightweight and consumption reducing damping material. The mechanical property of NBR hollow fibers aroused by changing NBR/PVC mass ratio and polymer mass fraction have been studied. The results show that the damping property of the hollow fiber structure is better than that of the plate membrane structure under the same conditions. The stretching and damping property of NBR hollow fiber can be optimized by changing NBR/PVC mass ratio and polymer mass fraction. The damping peak temperature of NBR hollow fiber decreases by increasing the NBR/PVC mass ratio. When polymer mass fraction is 25% and mass ratio of NBR/PVC is 80 - 20, the damping factor of NBR hollow fiber is the largest, which is 0.78.
参考文献
| [1] | Qin J J, Cao Y M, Oo M H. Preparation of poly(ether sulfone) hollow fiber UF membrane for removal of NOM [J]. Journal of Applied Polymer Science, 2006, 99(1): 430-435. |
| [2] | Chou W L, Yu D G, Yang M C.Influence of coagulant temperature and on-line drawing on the mechanical properties and permeation performance of cellulose acetate hollow fibers [J]. Journal of Polymer Research, 2005, 12: 219-229. |
| [3] | 李明俊, 李 蓉, 徐咏文, 等. 嵌入中空纤维的树脂基复合阻尼材料设计 [J]. 南昌航空大学学报, 2009, 23(2): 10-15. |
| [4] | 张世誉. 近年国内外丁腈橡胶发展态势分析 [J]. 弹性体, 2009, 19(1): 65-69. |
| [5] | Bower A F, Weiner J H. The role of pressure in rubber elasticity [J]. Journal of Chemical Physics, 2004, 24(120): 11948-11964. |
| [6] | 王 军, 奚旦立, 徐大同, 等. 聚氯乙烯中空纤维膜的研制 [J]. 膜科学与技术, 2002, 22(4): 7-12. |
| [7] | 王国全, 王秀芬. 聚合物改性 [M]. 北京: 中国轻工业出版社, 2009. |
| [8] | 符 刚, 张德志, 单国荣. 丁腈橡胶/聚氯乙烯共混物的阻尼性能 [J]. 合成橡胶工业, 2009, 32(4): 317-320. |
| [9] | 韩丽伟, 聂玉梅. 丁腈橡胶和聚氯乙烯共混合金隔振降噪阻尼性能研究 [J]. 化学工程师, 2003(2): 19-20. |
| [10] | Perera M C S, Ishiaku U S, Ishak Z A M. Characterization of PVC/NBR and PVC/ENR50 ternary blends by DMA and solid state NMR [J]. European Polymer Journal, 2001, 37(1): 167-178.. |
| [11] | 赵秀英, 向 平, 张立群. 受阻酚/丁腈橡胶复合材料的结构与性能 [J]. 复合材料学报, 2007, 24(2): 44-49. |
| [12] | 张 琦, 田 明, 吴友平, 等. 纳米氢氧化镁/橡胶复合材料的分散特性及分散机理 [J]. 复合材料学报, 2003, 20(4): 88-95.. |
| [13] | 向 平, 肖大玲, 赵秀英, 等. 受阻酚AO-80/NBR/PVC交联复合材料的结构与动态力学性能 [J]. 复合材料学报, 2007, 24(6): 44-49. |
| [14] | 何曼君, 张红东, 陈维孝, 等. 高分子物理 [M]. 3版. 上海: 复旦大学出版社, 2006. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%