The secondary hardening reaction is accompanied with precipitation of fine carbides in high CoNi ultrahigh strength steel.The crystal structure of the precipitating carbides is unambiguously determined by microbeam diffraction in transmission electron microscopy. It is identified that the needle-shaped carbides are M2C with a hexagonal structure. The concentration of substitutional alloying elements in the carbides quantified by energy dispersive X-ray spectroscopy (EDS) also supports the result above. The spatial structure of M2C is identical with L'3 type. Metal atoms are in a close packed hexagonal structure, the carbon atoms partly distribute with random in the octahedral interstices and the filling probability is less than 1/2. Particular attention was paid to the relationship of needle-shaped carbides/ferrite matrix at secondary hardening peak tempered at 482℃ for 5 h. Observation by high resolution transmission electron microscopy (HRTEM) confirms that carbides with black-white contrast are fully coherent with ferrite and have individual crystal structure, and the coarsened carbides with moire fringe are partially coherent with matrix. The orientation relationship between M2C and ferrite matrix is directly observed and identified with the well established P-S relationship [001]α //[111]c.
参考文献
[1] | V.K.Chandhok;J.P. Hirch;E.J.Dulis .[J].Transaction ASM,1963,56:677. |
[2] | J.J.IraniandR.W.K.Honeycome .[J].Iron and steel Institute,1965,203:826. |
[3] | D.Raynor;J.A.Whiteman;R.W.K.Honeycombe.[M].ISI,1966:349. |
[4] | V.K.Chandhok;J.P.Dulis .[J].Transaction ASM,1962,224:858. |
[5] | D.M.Daviesand.Ralph .[M].ISI,1972,201:262. |
[6] | D S Dakowski;P J Konkol;P Borough;L.F.Porter, M.Borough and A.M.Rathbone .[P].U S A Patent 3,502,462,1970. |
[7] | C D Little;P M Machmeier .[P].U:S:A Patent: 4 076 525,1978. |
[8] | R.M.Hemphill;D.E.Wert .[P].U:S:A Patent: 5 087 415,1992. |
[9] | G Olson.Proc 34th Sagamore Army Material Research Conf, ed GBOlson, US Army Materials Technology[J].Watertown MA,1990:3-66. |
[10] | 胡正飞,吴杏芳,梨秀球,王春旭.高CoNi合金钢中二次碳化物的析出与转化[J].金属学报,2001(04):381-385. |
[11] | R AyerandP M Machmeier .[J].Metallurgical and Materials Transactions,1998,29:903. |
[12] | ZhengfeiHU;Xingfang WU;Chunxu WANG .[J].Chin JMaterials res,2002,16:331. |
[13] | K W AndrewsandH Hughes.[M].ISI,1959:27. |
[14] | W Pearson.A Handbook of Lattice Spacings and Structure of Metals and Alloys[M].Pergamon Press,New York,1958 |
[15] | E PartheandV Sadagopan .[J].Acta Crystallographica,1963,16:202. |
[16] | A J Allen;D Gabillet;J R Weertman .[J].ACTA METALLURGICA ET MATERIALIA,1993,41:1969. |
[17] | G Olson;T J Kinkus;J S Montgomery .[J].Surface Science,1991,246:238. |
[18] | J.J.IraniandR.W.K.Honeycome .[J].IISI,1965,203:826. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%