采用金相显微镜、扫描电镜观察了经冲击疲劳试验后耐磨铸铁中碳化物的形貌、疲劳裂纹的萌生与扩展,测定了稀土含量及加热温度与裂纹的长度和裂纹扩展之间的关系曲线,在此基础上探讨了稀土变质及热处理对耐磨铸铁冲击疲劳性能的影响.结果表明: 稀土能推迟裂纹萌生的时间,降低裂纹扩展速率,提高其冲击疲劳抗力.当稀土与热处理共同作用时,效果更显著.其原因主要归于网状共晶碳化物形态与分布的改变.
参考文献
| [1] | Son Y W;Luo Q S;Chen Q D .Effect of RE-B modification on the strength and toughness of 30CrMn2Si cast steel[J].Journal of Materials Science,1994,29(06):1492. |
| [2] | Sari C;Waker C T;Kurate M .Interaction of U-Pu-Zr alloys containing minor actinides and rareearths with stainless steel[J].Journal of Nuclear Materials,1994,208(03):201. |
| [3] | Skok Y Y.New high-strength structural steels[J].Liteinoe Proizvodstvo,1992:36. |
| [4] | Sergeev A B;Starostin B M;Kofinana Y V.Technology for microalloying of steel and alloys[J].Metallurgiya,1996:31. |
| [5] | Yang Q X;Liao B;Liu J H .Effect of rare earth elements on austente growth dynamics of steel 60CrMnMo[J].Journal of Rare Earths,1998,16(03):274. |
| [6] | 姜启川;王树奇;崔向红 .稀土对铸造Cr12MOV模具钢碳化物形貌及性能的影响[J].中国稀土学报,1996,14(01):43. |
| [7] | 马前;刘白成;王兆昌 .Fe-C合金高温保温过程中碳化物表面的研究[J].钢铁,1994,29(05):47. |
| [8] | 马前;王兆昌 .白口铁热处理对共晶碳化物的溶解与粒状化[J].钢铁研究学报,1990,2(01):63. |
| [9] | 王树奇,姜启川,崔向红,何镇明.稀土对莱氏体钢共晶碳化物粒化的影响[J].中国稀土学报,1998(03):242-246. |
| [10] | 冯正.高浓度渗碳及其性能研究[J].热加工工艺,1994(06):11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%