制备了SiO2-Zr3(PO4)4改性的TiO2粉体,将其添加到陶瓷釉料中,研制出了TiO2光催化抗菌陶瓷,分别就改性TiO2粉体的光催化活性和TiO2光催化抗菌陶瓷的光催化抗菌机理进行了研究.研究表明,37.2%Zr3(PO4)4和11.5%SiO2改性的TiO2粉体经1323K处理后,仍具有较好的光催化活性,将其添加到陶瓷釉料中制备出的TiO2先催化抗菌陶瓷对大肠杆菌的抑菌率达98%.
TiO2 photocatalysis antibacterial ceramic was prepared by added TiO2 powder modified by SiO2-Zr3(PO4)4 in ceramic glaze. The photocatalysis mechanism of modified TiO2 powder and the photocatalysis antibac-terial mechanism of the ceramic have been investigated. Heat treated at 1323K, the modified TiO2 powder added 37.2% Zr3 (PO4)4 and 11.50%SiO2 showed a well photocatalysis activity,antibacterial ratio of the photocatalysis antibacterial ceramic to coliform have reached 98 %.
参考文献
| [1] | 梁金生 .[J].中国稀土学报,1999,17(zk):520-523. |
| [2] | 梁金生,金宗哲,王静.抗菌功能陶瓷材料的研究[J].河北工业大学学报,2000(05):45-47. |
| [3] | 项金钟,柳清菊,赵景畅,王毓德,刘焕林,吴兴惠,王儒林,陈再兴.抗菌建筑陶瓷研制[J].云南大学学报(自然科学版),2002(01):42-45. |
| [4] | Kikuchi Y;Sunada K;Iyoda T et al.[J].Journal of Photochemistry and Photobiology A:Chemistry,1997,106:51-56. |
| [5] | Sunada K;Kikuchi Y;Hashimoto K et al.[J].Environ Sci Tecnol,1998,32:726-728. |
| [6] | 黄惠莉,黄妙良,蔡阿娜,林煜,林文銮.TiO2光催化薄膜在陶瓷器具上抗菌效果的研究[J].应用化学,2002(01):48-52. |
| [7] | 李春红,陈玉清.纳米二氧化钛抗菌陶瓷内墙砖的研制和性能研究[J].陶瓷学报,2006(01):68-70. |
| [8] | 刘曙光,魏伟,郑庆新.抗菌、自清洁陶瓷的制备及性能表征[J].硅酸盐通报,2006(06):182-186. |
| [9] | 陈前林,吴建青,王龙现.SiO2的加入方法对高温稳定型纳米TiO2光催化活性的影响[J].中国陶瓷,2006(06):12-13,17. |
| [10] | 金效先;袁怡松;王承遇.玻璃工艺学[M].北京:中国轻工业出版社,1982:245. |
| [11] | 王绍亭;张远谋;范治新.化工传递过程[M].北京:化学工业出版社,1980:227-228. |
| [12] | 季君晖;史维明.抗菌材料[M].北京:化学工业出版社,2003:75-76,167. |
| [13] | 金宗哲.元机抗菌材料及应用[M].北京:化学工业出版社,2004:140. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%