建立了缝合复合材料层板在低速冲击载荷下的渐进损伤分析模型.模型中采用空间杆单元模拟缝线的作用;采用三维实体单元模拟缝合层板,通过基于应变描述的Hashin准则,结合相应的材料性能退化方案模拟层板的损伤和演化;采用界面单元模拟层间界面,结合传统的应力失效判据和断裂力学中的应变能释放率准则判断分层的起始和扩展规律.通过对碳800环氧树脂复合材料(T800/5228)层板的数值仿真结果和试验结果相比较,验证了模型的正确性,同时讨论了不同冲击能量下缝合层板的损伤规律.研究结果表明:缝线能够有效地抑制层板的分层损伤扩展;相同冲击能量下缝合与未缝合层板的基体损伤和纤维损伤在厚度分布上相似,缝合层板的损伤都要小于未缝合层板.
参考文献
| [1] | Rong MZ,Zhang MQ,Liu Y,et al.Effect of stitching on in plane and interlaminar properties of sisal/epoxy laminates[J].Journal of Composite Materials,2002,36(12):1505-1526.,2002. |
| [2] | Dransfield K,Baillie C,Mai Y W.Improving the delamina tion resistance of CFRP by stitching:a review[J].Composites Science and Technology,1994,50(3):305-317.,1994. |
| [3] | 程小全,郦正能,寇长河.缝合复合材料可用性--一般层合板的基本性能[J].复合材料学报,2004(04):71-76. |
| [4] | 李晨,许希武.缝合复合材料层板三维纤维弯曲模型及压缩强度预报[J].复合材料学报,2006(06):179-185. |
| [5] | 陈纲,桂良进,郦正能,寇长河.缝纫层合板低速冲击损伤有限元分析[J].航空学报,2002(01):55-58. |
| [6] | 程小全,赵龙,张怡宁.缝合复合材料可用性--简单层合板的基本性能[J].北京航空航天大学学报,2003(11):1001-1005. |
| [7] | Aymerich F,Pani C,Priolo P.Effect of stitching on the low velocity impact response of【03903】s graphite/epoxy lami nates[J].Composites Part A:Applied Science and Manufac turing,2007,38(4):1174-1182.,2007. |
| [8] | Aymerich F,Pani C,Priolo P.Damage response of stitched cross ply laminates under impact loadings[J].Engineering Fracture Mechanics,2007,74(4):500-514.,2007. |
| [9] | Aymerich F,Priolo P.Characterization of fracture modes in stitched and unstitched cross ply laminates subjected to low velocity impact and compression after impact loading[J].In ternational Journal of Impact Engineering,2008,35(7):591-608.,2008. |
| [10] | 毛春见,许希武,郑达.缝合复合材料层板低速冲击及冲击后压缩实验研究[J].复合材料学报,2012(02):160-166. |
| [11] | Liu D.Delamination resistance in stitched and unstitched composite plates subjected to impact loading[J].Journal of Reinforced Plastics and Composites,1990,9(1):59-69.,1990. |
| [12] | Lopresto V,Melito V,Leone C,et al.Effect of stitches on the impact behaviour of graphite/epoxy composites[J].Composites Science and Technology,2006,66(2):206-214.,2006. |
| [13] | Hashin Z.Fatigue failure criteria for unidirectional fiber com posites[J].ASME,Transactions,Journal of Applied Me chanics,1981,48:846-852.,1981. |
| [14] | Camanho P P,Matthews F L.A progressive damage model for mechanically fastened joints in composite laminates[J].Journal of Composite Materials,1999,33(24):2248-2280.,1999. |
| [15] | Pedro P C,Carlos G D.Mixed mode decohesion finite ele ments for the simulation of delamination in composite Mater als,NASA/TM-2002-211737[R].Washington:NASA,2002.,2002. |
| [16] | 陈蔚.缝纫增强复合材料冲击损伤与冲击后压缩破坏研究[J].航空材料学报,1997(04):49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%