研究了以生物模板(木炭)浸渍TiO2溶胶,高温碳热-氮化制备TiN陶瓷的工艺过程.应用热力学原理计算了经溶胶浸渍后形成的TiO2/C复合体系的氮化条件,确定了N2,CO分压对氮化温度的影响.采用碳热氮化法,在高浓度的氮气压力下反应烧结制备了具有生物形貌的多孔TiN/C陶瓷.结果表明:在1400℃,4 h,0.5 MPa氮气压力下,得到了具有立方晶体结构的TiN/C多孔陶瓷,并保留了木材模板的显微结构.
参考文献
| [1] | Shin Y S;Liu J;Chang J H et al.[J].Advanced Materials,2001,13(10):728. |
| [2] | Ramnbo C R;Martinelli J R .[J].ADVANCED POWDER TECHNOLOGY,2001,189:19. |
| [3] | Huang J G;Kunitake T .[J].Journal of the American Chemical Society,2003,125(39):11834. |
| [4] | He J H;Kunitake T;Watanabe T.[J].CHEMISTRY COMMUNICATIONS,2005(06):795. |
| [5] | Davis S A;Burkett S L;Mendelson N H et al.[J].Nature,1997,385(6615):420. |
| [6] | Mao C B;Solis D J;Reiss B D et al.[J].Science,2004,303(5655):213. |
| [7] | Braun E;Eichen Y;Sivan U et al.[J].Nature,1998,391(6669):775. |
| [8] | 乔冠军,金志浩.用木材制备生物结构陶瓷[J].材料导报,2003(04):66-69. |
| [9] | Vogli E;Sieber H;Greil P .[J].Journal of the European Ceramic Society,2002,22(14-15):2663. |
| [10] | Sieber H;Vogli E;Mullier F et al.[J].Euro Ceramics Vii,2002,206(Pt1-3):22013. |
| [11] | 钱军民,王继平,金志浩.液相渗入-反应法制备木材结构SiC的研究[J].稀有金属材料与工程,2004(10):1065-1068. |
| [12] | Sun B H;Fan T X;Zhang D et al.[J].CARBON,2004,42(01):177. |
| [13] | Ramnbo C R;Cao J;Rusina O et al.[J].Carbon,2005,43(06):1174. |
| [14] | Ota T;Imaeda M;Takase H et al.[J].Journal of the American Ceramic Society,2000,83(06):1521. |
| [15] | Rambo C R;Sieber H .[J].Advanced Materials,2005,17(08):1088. |
| [16] | Rambo CR;Cao J;Sieber H .Preparation and properties of highly porous, biomorphic YSZ ceramics[J].Materials Chemistry and Physics,2004(2/3):345-352. |
| [17] | 吴义权,张玉峰,郭景坤.Ti-N-C-O系的热力学分析与相平衡[J].硅酸盐通报,2000(06):46-49. |
| [18] | 叶大伦.实用无机物热力学数据手册[M].北京:冶金工业出版社,1981:66. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%