利用扫描电子显微镜和能谱仪分析Cu对Ag-Ce合金组织与结构的影响。结果表明：Ag-Cu-Ce合金基体为银铜固溶体，晶粒较小，基体上弥散分布着恀多共生析出的β-Cu和Ag4Ce颗粒，Cu的加入改善了Ag4Ce的偏析现象。Ag-Ce和Ag-Cu-Ce合金的拉伸断口呈锥形，有明显的韧窝组织，为典型的韧性断裂。
The effects of Cu addition on the microstructure of Ag-Ce alloy were studied by SEM and EDS. The results showed that the main body of Ag-Cu-Ce alloys is silver-copper solid solution with smaller crystal grains, in which many symbiotically separated β-Cu and Ag4Ce particles were distributed diffusively. Cu addition segregation. Tensile fracture of Ag-Ce and Ag-Cu-Ce alloys was shown cone and left distinct tough pit, which is typical tough break.
参考文献
| [1] | 黄子高 .银铈合金应用实践[J].贵金属,1985,6(04):49-51. |
| [2] | 杨应魁,费家祥,王永根.AgCe电触头材料线材的制备[J].电工材料,2005(03):15-18. |
| [3] | 赵怀志.银铈电接点材料的研究[J].稀土,1981(01):28. |
| [4] | 贺晓燕,周世平,王健,乔勋,俞健树,裴洪营,马云秋.Cu对AgCe合金机械性能及再结晶温度的影响[J].贵金属,2008(02):11-14. |
| [5] | 贺晓燕,周世平,王健,乔勋,王光庆,吕飞.Cu对Ag-0.5Ce触头电弧侵蚀形貌特征的影响[J].贵金属,2009(01):17-21. |
| [6] | 石路,李晋霞,王佳夫,王继周,刘刚,王艳杰.复合稀土银合金组织与性能的研究[J].铸造,2003(01):28-32. |
| [7] | 杨玉璐 .银铈合金的金相与分析[J].贵金属,1985,6(02):11-14. |
| [8] | 左演声;陈文哲;梁伟.材料现代分析方法[M].北京:北京工业大学出版社,2003:173. |
| [9] | 张康候;陈黎莉;何纯孝 .Ag-Cu-Ce 三元系相图的500℃等温截面[J].中国稀土学报,1993,11(03):268-270. |
| [10] | 何纯孝,张康侯,陈藜莉.Ag-Cu-RE合金相图固溶度及成相规律[J].贵金属,1994(03):25-28. |
| [11] | 赵品;谢辅洲;孙振国.材料科学基础教程[M].哈尔滨:哈尔滨工业大学出版社,2002:142. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%