收集了临床中拆除的镍铬合金烤瓷冠,按佩戴年限分为1年组、2年组、34年组、5～9年组、10年以上组,并设立对照组.采用接触角仪测定各组试样的接触角,利用电化学工作站测试电化学腐蚀曲线,应用扫描电镜观察试样表面腐蚀形貌,并进行统计学分析.结果表明,1年组试样腐蚀电位及腐蚀电流密度相对较小,2年组试样腐蚀电位和腐蚀电流密度增加并显著高于其它组,3～5年组、5～10年组、10年以上组试样腐蚀电位及腐蚀电流密度相对2年组逐渐减小,这种变化趋势与接触角测试结果一致.随佩戴年限的增加,镍铬烤瓷内冠的腐蚀程度越来越严重,即镍铬合金烤瓷冠在口腔内存在腐蚀,且佩戴2年左右时腐蚀速度最快,腐蚀程度随年限增加累积.因此,口腔临床中应采取积极的措施预防镍铬合金烤瓷冠的早期腐蚀.
参考文献
| [1] | Wataha J C,Malcolm C T,Hanks C T.Correlation between cyto-toxicity and elements released by dental casting alloys[J].Int J Prothodont,1995,8(1):9 |
| [2] | 李相波,王伟,王佳等.水中微生物膜的生长对金属腐蚀过程的影响[J].腐蚀科学与防护技术,2002,14(4):218 |
| [3] | Wataha J C,Lockwood P E,Khajotia S S,et al.Effect of pH on element release from dental casting alloys[J].J Prosthet.Dent.,1998,80(6):691 |
| [4] | Edwards D L,Wataha J C,Hank C T.Uptake and reversibility of uptake of nickel by human marcophages[J].J.Oral Rehabil.,1998,25(1):2-7 |
| [5] | Roach M D,Wolan J T,Parsell D E.Use of X-ray photoelectron spectroscopy and cyclic polarization to evaluate the corrosion behavior of six nickel-chromium alloys before and after porcelain-fused-to-metal firing[J].J Prosthet.Dent.,2000,84(6):623 |
| [6] | 苏剑生,余懿强,王涛.牙科铸造合金的离子释出及生物学性能的研究现状[J].口腔材料器械杂志,2005,14(3):146 |
| [7] | 谢立莉,李玉玲.金属烤瓷修复体牙龈缘变色的电化学腐蚀因素研究[J].广西医学,2008,30(5):682 |
| [8] | 杜娟,张信岳.镍铬合金烤瓷修复体的生物安全性研究进展[J].医学综述,2010,16(10):1512 |
| [9] | 樊灿灿,宁静,刘斌等.镍铬合金烤瓷牙的肾毒性:理论研究与临床验证[J].中国组织工程研究与临床康复,2010,14(3):517 |
| [10] | 王佩,章海宁,陈德福等.镍铬合金烤瓷冠修复后患者血液和尿液镍铬元素含量检测分析[J].河北医药,2011,33(12):1831 |
| [11] | Li R Q,Kan H X,Zheng Z F.Effects of Ni-Cr based porcelain-fused-to-metal crown on periodontal tissue[J].J.Clin.Rehabil.Tissue Eng.Res.,2009,13(25):4990 |
| [12] | 张荣和,宋琦,张勇.镍铬合金烤瓷冠冠组织面离子析出的研究[J].国际口腔医学杂志,2008,35:611 |
| [13] | Wang L,Zhang J,Zeng Z,et al.Fabrication of a nancrystatline Ni-Co/CoO functionally graded layer with excellent electrochemical corrosion and tribological performance[J].Nanotechnology,2006,17:4614 |
| [14] | Roach M D,Wolan J T,Parsell D E.Use of X-ray pho-toelectro spectroscopy and cyclic polarization to evaluate the corrosion behavior of six nickel-chromium alloys before and after porcelain-fused-to-metal firing[J].J.Prosthet.Dent.,2000,84(6):623 |
| [15] | Cai Z,Vermilyea S G,Brantley W A.In vitro corrosion resistance of high-palladium dental casting alloys[J].Dent.Mater.,1999,15(3):202 |
| [16] | 崔志峰,韩一纯,庄力健等.在Cl-环境下金属腐蚀行为和机理[J].石油化工腐蚀与防护,201 1,28(4):1 |
| [17] | 胡滨,张富强.镍铬合金在人工唾液中的电化学腐蚀行为[J].中华口腔医学杂志,2003,38(2):140 |
| [18] | 李玉玲,谢立莉.不同修复时间的镍铬合金烤瓷冠龈缘状况及内冠边缘扫描电镜观察[J].广西医科大学学报,2010,27(2):220 |
| [19] | Cai Z,Vermilyea S G,Brantley W A.In vitro corrosion resistance of high-palladium dental casting alloys[J].Dent.Mater.,1999,15(3):202 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%