采用电弧炉快淬和晶化退火工艺制备高性能NdxFe90.5-xZr3.0B6.5(x=8.5~11.5)快淬磁体.结果表明,Zr的添加显著提高磁体的磁性能,Nd含量可以明显提高磁体的磁性能,x由8.5增加到10.5时,NdxFe90.5-xZr3.0B6.5磁体的磁能积由75 kJ/m3升高到114 kJ/m3,接近于美国Magnequench公司的MQP-B磁粉性能.
参考文献
[1] | Coehoorn R;Mooij D B;Duchateau J P W B et al.[J].Journal de Physique,1988,49(C8):669. |
[2] | Chang WC.;Wu SH.;Ma BM.;Bounds CO.;Chiou DY. .High performance alpha-Fe/Nd2Fe14B-type nanocomposites[J].Applied physics letters,1998(1):121-123. |
[3] | Zhang WY.;Cheng ZH.;Zhang SY.;Shen BG.;Zhang J. .Microstructure refinement and improvements of magnetic properties of Pr-2(Fe, Co)(14)B/alpha-(Fe, Co) nanocomposites by additional Ga[J].Journal of Physics. Condensed Matter,2001(17):3859-3864. |
[4] | Fukunaga H;Nakamura H .[J].Scripta Materialia,2001,44:1341. |
[5] | Wang ZC.;Li FB.;Zhou SZ.;Wang R.;Gong W.;Zhang MC. .HIGH-COERCIVITY (NDDY)(2)(FENB)(14)B-ALPHA-FE NANOCRYSTALLINE ALLOYS[J].Journal of Applied Physics,1997(8 Pt.2b):5097-5099. |
[6] | Yin J H;Zhou Y X;Tang S L et al.[J].Journal of Applied Physics,1999,85:7336. |
[7] | Wang ZC.;Zhang MC.;Qiao Y.;Zhou SZ. .High-performance alpha-Fe/Pr2Fe14B-type nanocomposite magnets produced by hot compaction under high pressure[J].Journal of Applied Physics,2000(1):591-593. |
[8] | Chang WC.;Hsing DM. .MAGNETIC PROPERTIES AND TRANSMISSION ELECTRON MICROSCOPY MICROSTRUCTURES OF EXCHANGE COUPLED ND12-XFE82+XB6 MELT SPUN RIBBONS[J].Journal of Applied Physics,1996(8 Pt.2a):4843-4845. |
[9] | Harland CL.;Davies HA. .Effect of Co and Zr on magnetic properties of nanophase PrFeB alloys[J].Journal of Applied Physics,2000(9 Pt.3):6116-6118. |
[10] | Schrefl T;Fidler J;Kronmuller H .[J].Physical Review B,1994,49:6100. |
[11] | 范雄.金属X射线学[M].北京:机械工业出版社,1998:103. |
[12] | Bauer J.;Zern A.;Kronmuller H.;Seeger M. .NANOCRYSTALLINE FENDB PERMANENT MAGNETS WITH ENHANCED REMANENCE[J].Journal of Applied Physics,1996(3):1667-1673. |
[13] | Wu YQ.;Ping DH.;Xiong XY.;Hono K. .Magnetic properties and microstructures of alpha-Fe/Nd2Fe14B nanocomposite microalloyed with Zr[J].Journal of Applied Physics,2002(10 Pt.3):8174-8176. |
[14] | 刘建华,张朋越,杨丽,谌岩,关颍,张克勤,张静武,张湘义.Zr对Pr-Fe-B非晶合金晶化形成纳米晶合金的作用[J].功能材料,2002(03):260-261. |
[15] | Ravippasad K;Ravishankarn N;Chattopadhyay K et al.[J].Journal of Applied Physics,1998,83:916. |
[16] | Manaf A.;Zhang P.Z. .Magnetic properties and microstructural characterisation of isotropic nanocrystalline Fe-Nd-B based alloys[J].IEEE Transactions on Magnetics,1993(6):2866-2868. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%