研究了95W-3.5Ni-1.5Fe合金在400～1100℃范围内的高温拉伸力学性能及其断口特征,并分析了其断裂机制.结果表明:合金的抗拉强度及屈服强度均随温度升高而降低,延伸率和断面收缩率随温度升高呈现先增加后降低的关系,600℃时延伸率和断面收缩率达到最大值.对其断口分析结果表明:在400～600℃范围内,由于钨相发生了塑脆转变,钨颗粒塑性提高使得两相协调变形能力增强,合金塑性提高.而当温度升高到700℃以上,粘结相发生动态再结晶软化,钨相和粘结相界面结合强度大幅度下降,外加应力不能由粘接相传递到钨颗粒,其两相协调变形能力变差,导致合金强韧性急剧下降.
参考文献
| [1] | 范景莲.Tungsten Heavy Alloy and New Fabricating Technology(钨合金及其制备新技术)[M].北京:冶金工业出版社,2006 |
| [2] | Fan J L;Gong X;Huang B Y et al.[J].Mechanics of Materials,2010,42:24. |
| [3] | 罗述东,易健宏,王太宏,唐新文.80W-10Ta-7Ni-3Fe高密度合金研究[J].稀有金属材料与工程,2005(02):226-230. |
| [4] | Fan Jing-lian;Liu Tao;Cheng Hui-chao;Wang Deng-long .Preparation of fine grain tungsten heavy alloy with high properties by mechanical alloying and yttrium oxide addition[J].Journal of Materials Processing Technology,2008(1/3):463-469. |
| [5] | Yu Yang;Hu Lianxi;Wang Erde .Microstructure and mechanical properties of a hot-hydrostatically extruded 93W-4-.9Ni-2.1Fe alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(0):620-624. |
| [6] | 范景莲,黄伯云.钨合金的形变强化新工艺与断裂机制研究[J].硬质合金,2007(02):119-123. |
| [7] | 于洋,王尔德,胡连喜,张宝友,于杰.形变强化对93W-4.9Ni-2.1Fe合金组织及性能的影响[J].材料科学与工艺,2005(04):442-444,448. |
| [8] | Gero R;Borukhin L;Pikus I .[J].Materials Science and Engineering,2001,A302:162. |
| [9] | 房文斌,王尔德,于洋.95W-5（Ni/Fe/Co）合金高温变形及影响因素[J].稀有金属材料与工程,2005(08):1247-1250. |
| [10] | 徐英鸽;康进兴;陈文涛 et al.[J].材料热处理学报,2006,35(14):1. |
| [11] | Hollomorl J H .[J].Transactions of ASM,1994,32:123. |
| [12] | Erwin Pink;Subodh Kumar;Robert Grill .[J].International Journal of Refractory Metals and Hard Materials,1997,15:301. |
| [13] | Karl Heinz Matucha.Materials Science and Technology (Vol.8)(材料科学与技术丛书,第八卷)[M].Bei.jing:Science Press,1999:529. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%