The structure and properties of nanocrystalline PVC were investigated. The crystalline region of nanocrystalline PVC was observed by TEM to be 80 nm. The melting point of nanocrystalline PVC was found to be 128℃ which is obviously lower than typical PVC (210℃). The X-ray diagram indicated that the crystal existed in nanocrystalline PVC. The evident effect of self-plasticizing and reinforcement appeared when nanocrystalline PVC was added. The optimum amount for self-plasticizing is about 10%. The maximal impact strength of 95.1 kJ/m2 was achieved by adding 20% nanocrystalline PVC and tensile strength with 56.2 MPa which was 122% of pure PVC was obtained after adding 5% nanocrystalline PVC.
参考文献
| [1] | ECrawford;JLesser .[J].Journal of Polymer,2000,41:5865. |
| [2] | YNakamura;MKanbe;ETakekuni .[J].Comps Interf Netherls,2001,8:367. |
| [3] | CMChan;SHZhu;SCWong;YWMai .[J].Journal of Polymer Materials Science and Engineering,1999,39:1998. |
| [4] | SMishra;GBPerumal;JBNaik .[J].Journal of Polym Plast Technol Eng,1997,36:489. |
| [5] | SZhu;CChan;SWong;YMai .[J].Journal of Polymer Materials Science and Engineering,1999,39(10):1998. |
| [6] | XiaomingLiu.Modification Processing of Rigid PVC[M].北京:中国轻工业出版社,1998:78. |
| [7] | MGilert;KEAnsari .[J].Journal of Applied Polymer Science,1982,27:2553. |
| [8] | HWang;MMei;YJiang;QLi, XZhang , SWu .[J].Journal of Polym Intern,2002,51:7. |
| [9] | ERuckenstein;YMYuan .[J].Polymer,1997,39(15):3855. |
| [10] | Misi;CNicolella;EPalazzi;MRovatti ,GFerraiolo .[J].Chemical Engineering and Technology,1994,17:67. |
| [11] | CXXiong;TWang .[J].Journal of Applied Polymer Science,2004,91(01):563. |
| [12] | RAMarshall .[J].Journal of Vinyl Technology,1994,16(01):35. |
| [13] | FengShengli.Application , Manufacture Technology of Special Superfine Power[M].北京:国防工业出版社,2002:28. |
| [14] | RGJin;YQHua .[J].Journal of Polymer Science Part B:Polymer Physics,1991,29:101. |
| [15] | SYGuo;XXu.[J].Journal of Polymer Materials Science and Engineering,1993(06):106. |
| [16] | SYGuo;XXu.[J].Journal of Polymer Materials Science and Engineering,1995(02):81. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%