借助显微硬度计、光学显微镜、扫描电镜、X射线衍射分析、腐蚀实验和拉伸测试等手段,研究了锆、锶复合微合金化铸态镍铝青铜的硬度、组织、耐蚀性能和力学性能.结果表明:与未微合金化铸态镍铝青铜(Cu-8.87Al-5.22Fe-4.48Ni-1.08Mn-0.53Zn)相比,锆、锶复合微合金化铸态镍铝青铜(Cu-9.86Al-5.84Fe-4.46Ni-1.03Mn-0.6Zn-0.048Zr-0.03Sr)的相组成没有显著变化,都由α相、β相、γ2相和κ相组成.但是微合金化镍铝青铜的α相和κⅣ相显著细化,共析组织(α相+κⅢ相)也大幅细化,合金硬度从212.1 HV提高到216 HV.由于腐蚀优先发生在共析区域内,而共析组织的细化降低了其产生连续腐蚀通道的概率,促进了合金的均匀腐蚀性能和电化学腐蚀性能的全面提高(在3.5％ NaCl水溶液中均匀腐蚀速率和电化学腐蚀速率分别降低2.9％和49.6％);晶粒细化和颗粒弥散强化提高了微合金化镍铝青铜的力学性能,其抗拉强度和屈服强度分别提高到676.6 MPa和260.3 MPa(分别提高4.06％和4.07％).
参考文献
| [1] | 郭泽亮,方亮,汤文新.海水泵用铜合金的腐蚀性能评述[J].材料导报,2003(08):22-24. |
| [2] | 刘平,任凤章,贾淑果.铜合金及其应用[M].北京:化学工业出版社,2007.,2007. |
| [3] | JB/T 7901-1999.金属材料实验室均匀腐蚀全浸试验方法[S].北京:北京工业仪器仪表综合技术研究所,2001.,2001. |
| [4] | 路阳,袁利华,李文生,等 .高铝青铜Cu-14% Al-X合金在3.5%NaCl溶液中的腐蚀性能[J].机械工程学报,2005,41(9):42-45.LU Yang,YUAN Li-hua,LI Wen-sheng,et al.Corrosion resistance of Cu-14% Al-XAl-bronze alloy in 3.5% NaCl solution[J].Chinese Journal of Mechanical Engineering,2005,41 (9):42-45.,2005. |
| [5] | 李文生,王智平,路阳,等 .高铝青铜Cu-14Al-X合金在3.5%NaCl溶液中的腐蚀行为[J].中国有色金属学报,2006,16(3):511-517.LI Wen-sheng,WANG Zhi-ping,LU Yang,et al.Corrosion behavior of Cu-14Al-X bronze alloy in 3.5% NaCl solution[J].The Chinese Journal of Nonferrous Metals,2006,16(3):511-517.,2006. |
| [6] | 宋德军,孙现龙,许磊,叶景涛,胡伟民.变形镍铝青铜合金的组织研究[J].稀有金属,2008(04):420-424. |
| [7] | 许晓静,王彬,吴桂潮,等 .锶微合金化高锌2099型铝合金抗晶间腐蚀及剥蚀性能[J].稀有金属材料与工程,2011,40:248-251.XU Xiao-jing,WANG Bin,WU Gui-chao,et al.Intergranular corrosion and exfoliation corrosion properties of strontium microalloyed 2099 type aluminum alloy with high zinc content[J].Rare Metal Materials and Engineering,2011,40(S2):248-251.,2011. |
| [8] | 张文奇,石声泰,肖纪美.金属腐蚀手册[M].上海:上海科学技术出版社,1987.,1987. |
| [9] | Al-Hashem A,Riad W .The role of microstructure of nickel-aluminium-bronze alloy on its cavitation corrosion behavior in natural seawater[J].Materials Characterization.2002,2002,48(1):37-41.,2002. |
| [10] | Fonlupt S,Bayle B,Delafosse D,et al .Role of second phases in the stress corrosion cracking of a nickel-aluminium bronze in saline water[J].Corrosion Science,2005,47(11):2792-2806.YU Hong,ZHENG Yu-gui,YAO Zhi-ming,et al.Cavitation erosion behavior of a cast nickel-aluminum bronze in 2.4% NaCl solution【J】.Corrosion Science and Protection Technology,2007,19(3):181-185.,2005. |
| [11] | 于宏,郑玉贵,姚治铭,于春洋.ZQAl9-4-4-2镍铝青铜在2.4%NaCl溶液中的空蚀行为[J].腐蚀科学与防护技术,2007(03):181-185. |
| [12] | 王剑钊,王少华,房灿峰,杨守杰,戴圣龙,孟令刚,张兴国.Zr对2E12铝合金显微组织和力学性能的影响[J].中国有色金属学报,2009(02):247-251. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%