研究了Gd5Si1.975Ge1.975T0.05(T为Ni、Mn、Cr、Co、Fe)合金的结构及磁热效应.XRD结果显示:当T元素的原子序数为偶数时,合金形成了单一的Gd5Si2Ge2单斜结构;而当原子序数为奇数时,则为Gd5Si2Ge2单斜结构和正交结构的混合相.在拥有单一相的合金中均发现了巨磁热效应,然而在具有混合相的合金中由于未能发生一级结构相变而导致了低的磁熵变.此外,Gd5Si1.975Ge1.975Cr0.05合金的磁制冷量达到了112 J/kg,相对于Gd5Si2Ge2合金提高了50%.
参考文献
| [1] | Zimm C et al.[J].Advances in Cryogenic Engineering,1998,43:1759. |
| [2] | Pecharsky VK;Gschneidner KA .Tunable magnetic regenerator alloys with a giant magnetocaloric effect for magnetic refrigeration from similar to 20 to similar to 290 K[J].Applied physics letters,1997(24):3299-3301. |
| [3] | Hu F X;Shen B G;Sun J R et al.[J].Applied Physics Letters,2001,78:3675. |
| [4] | Tegus O;Bruck E;Buschow K H J et al.[J].Nature,2002,415:450. |
| [5] | Provenzano V;Shapiro A J;Shull R D .[J].Nature,2004,429:853. |
| [6] | Enyao Zhang;Yungui Chen;Tiebang Zhang et al.[J].Journal of Magnetism and Magnetic Materials,2006,301:410. |
| [7] | Gschneidner K A.[J].Materials Science Forum,1999(315-317):69. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%