高级检索

对AZG315镁合金在540℃进行不同时间固溶处理,研究了其显微组织的演变.通过OM、SEM、EDS、XRD对合金显微组织和相组成进行了表征.结果表明,AZG315镁合金中主要含有两种相,一种为α-Mg基体相,另一种为Al2 Gd第二相.在固溶处理的过程中,随固溶时间延长,Al2Gd相的形貌发生显著的变化,由铸态下的针状逐次变为棒状、短杆状、颗粒状.然而,这种形貌的演变恰好符合Ostwald熟化理论,并且当固溶时间为16 h时,A12 Gd颗粒相近乎均匀分布在基体中,可以有效的起到第二相强化作用.

Microstructure evolution of AZG315 magnesium alloy during solution treatment at 540 ℃ was investigated.The microstructure and phase composition were characterized by OM,SEM,EDS analysis and XRD.The results indicate that two phases mainly exist in AZG315 alloy.One is α-Mg matrix and the other is Al2Gd phase.In the process of solution treatment,the morphology of the Al2Gd phase changes enormously.The morphology of the Al2Gd phase is needle shape,rod-like,short-bar shape and granular in turn during the solution treatment,which conforms with Ostwald ripening theory.The morphology of the Al2Gd phase becomes granular and it is distributed in the matrix uniformly after solution treatment for 16 h,which results in the efficient strengthening from the second phase.

参考文献

[1] 张丁非;张红菊;兰伟;马春华.高强镁合金的研究进展[J].材料热处理学报,2012(6):1-8.
[2] 卢立伟;赵俊;刘龙飞;陈志钢;刘天模.镁合金大塑性变形的研究进展[J].材料热处理学报,2014(z1):1-7.
[3] 王社斌;李晓斌;范晋平;王帅;许并社.Mg-5Al-0.8Ca-0.2La-xSr合金的显微组织及高温力学性能[J].中国有色金属学报,2009(5):826-832.
[4] 曾小勤;吴玉娟;彭立明;林栋樑;丁文江;彭赢红.Mg-Gd-Zn-Zr合金中的LPSO结构和时效相[J].金属学报,2010(9):1041-1046.
[5] 张金玲;冯芝勇;胡兰青;王社斌;许并社.不同La含量AZ91合金的时效硬化行为[J].金属学报,2012(5):607-614.
[6] R. Mahmudi;F. Kabirian;Z. Nematollahi.Microstructural stability and high-temperature mechanical properties of AZ91 and AZ91 + 2RE magnesium alloys[J].Materials & design,20115(5):2583-2589.
[7] X.B. Liu;R.S. Chen;E.H. Han.Effects of ageing treatment on microstructures and properties of Mg-Gd-Y-Zr alloys with and without Zn additions[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20081/2(1/2):232-238.
[8] 王社斌;祁小叶;张金玲;刘璐;许并社.时效处理和La含量对AZ91合金组织和力学性能的影响[J].金属学报,2011(6):743-750.
[9] Sun, Ming;Hu, Xiaoyu;Peng, Liming;Fu, Penghuai;Peng, Yinghong.Effects of Sm on the grain refinement, microstructures and mechanical properties of AZ31 magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2015:89-96.
[10] Xudong Wang;Wenbo Du;Ke Liu.Microstructure, tensile properties and creep behaviors of as-cast Mg-2Al-1Zn-xGd (x = 1, 2,3, and 4 wt.%) alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2012:78-84.
[11] Wang, X.;Du, W.;Wang, Z.;Liu, K.;Li, S..Microstructures and mechanical properties of quasicrystal reinforced AZ31 matrix composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011:446-451.
[12] Lu, Fumin;Ma, Aibin;Jiang, Jinghua;Guo, Yu;Yang, Donghui;Song, Dan;Chen, Jianqing.Significantly improved corrosion resistance of heat-treated Mg-Al-Gd alloy containing profuse needle-like precipitates within grains[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2015May(May):171-178.
[13] Junjie Li;Wei Liu.Effects of high magnetic field on isothermal pearlite transformation and microstructure in a hypereutectoid steel[J].Journal of Magnetism and Magnetic Materials,2014:159-164.
[14] Ai, Cheng;Zhao, Xinbao;Zhou, Jian;Zhang, Heng;Liu, Lei;Pei, Yanling;Li, Shusuo;Gong, Shengkai.Application of a modified Ostwald ripening theory in coarsening of gamma ' phases in Ni based single crystal superalloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2015:558-562.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%