从分子结构设计出发,采用二乙炔基苯、苯基二氯硼烷和甲基氢二氯硅烷为主要原料,采用格氏试剂法合成了一种耐高温硼硅炔有机-无机杂化树脂聚(二乙炔基苯-硅烷-硼烷)(PASB).采用FT-IR、1H-NMR、13C-NMR和GPC对其结构进行了表征,利用DSC和TGA研究了聚合物的固化反应行为和耐热性能,讨论了结构中不同硅硼含量与产物性能之间的依赖关系.结果表明,PASB树脂常温下黏度适中,可以在较低的温度下发生固化交联反应,具有良好的加工性能.其固化物具有良好的耐热性,在N2气氛下失重5％时的温度(Td5)均高于600℃,1000℃的质量保留率大于85％.
参考文献
| [1] | Homrighausen CL.;Keller TM. .Synthesis and characterization of a silarylene-siloxane-diacetylene polymer and its conversion to a thermosetting plastic[J].Polymer: The International Journal for the Science and Technology of Polymers,2002(9):2619-2623. |
| [2] | Zhou Q;Feng X;Ni LZ;Chen JD .Novel heat resistant methyl-tri(phenylethynyl)silane resin: Synthesis, characterization and thermal properties[J].Journal of Applied Polymer Science,2006(3):2488-2492. |
| [3] | Zhou Q;Mao ZJ;Ni LZ;Chen JD .Novel phenyl acetylene terminated poly(carborane-silane): Synthesis, characterization, and thermal property[J].Journal of Applied Polymer Science,2007(4):2498-2503. |
| [4] | Cheng, R.;Zhou, Q.;Ni, L.;Chen, Y.;Wang, J. .Synthesis and thermal property of boron-silicon- acetylene hybrid polymer[J].Journal of Applied Polymer Science,2011(1):47-52. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%