以高岭土、SiC粉末、Al2O3粉末为主要原料,采用添加造孔剂法制备了SiC/莫来石复相多孔陶瓷,探讨了烧结温度对多孔陶瓷的气孔率、体积密度、抗折强度等的影响.分别采用X射线衍射仪(XRD)、扫描电子显微镜( SEM)表征了样品的物相组成与断面形貌.结果表明,以淀粉为造孔剂,在1350℃下保温2h制备的样品综合性能最佳,其孔隙率为31.40％,抗折强度达到42.50MPa.
参考文献
| [1] | 张锐.The porosity and strength of SiC porous ceramics(碳化硅多孔陶瓷的气孔率和强度)[J].金刚石与磨料磨具工程,2000(04):38. |
| [2] | 梁训裕;刘景林.碳化硅耐火材料[M].北京:冶金工业出版社,1981:126. |
| [3] | Aksay I A;Dabbs D M;Sarikaya M .Mullite for structural,electronic,and optical application[J].Journal of the American Ceramic Society,1991,74(10):2343. |
| [4] | Weiguang Chi;Dongliang Jiang;Zhengren Huang .Sintering behavior of porous SiC ceramics[J].Ceramics International,2004(6):869-874. |
| [5] | 张锐,高濂,程国峰,郭景坤.注浆成型SiC多孔陶瓷的工艺和性能研究[J].无机材料学报,2002(04):725-730. |
| [6] | Kim B H;Na Y H .Fabrication fiber-reinforced porous ceramics of Al2O3-mullite and SiC mullite system[J].Ceramics International,1995,21(06):381. |
| [7] | Tian J;Shobu K .Fracture strength of melt-infiltrated SiC-mullite composite[J].Journal of Materials Science,2004(11):3751-3755. |
| [8] | Schwartzwalder K;Somers A V .Method of making porous ceramic articles[P].US 3090094,1963-05-21. |
| [9] | 韩永生,李建保,魏强民.多孔陶瓷材料应用及制备的研究进展[J].材料导报,2002(03):26-29. |
| [10] | 常春,陈传忠,孙文成.SiC的高温抗氧化性分析[J].山东大学学报(工学版),2002(06):581-585. |
| [11] | 刘岩,黄政仁,董绍明,姚秀敏,江东亮.碳化硅泡沫陶瓷浆料成分与烧结性能[J].无机材料学报,2005(02):305-309. |
| [12] | 李如椿.莫来石结合碳化硅制品的研制[J].河北理工学院学报,2001(04):51-54. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%