稀土被认为是金属中的"维他命",在钎料中添加微量的稀土Ce可以显著地改善钎料合金的综合性能.然而,当钎料中添加过量的稀土时,将会发现Sn晶须的快速生长现象.结果表明,如果将Sn3.8Ag0.7Cu1.0Ce钎料内部的稀土相暴露于空气中,稀土相将发生氧化而产生体积膨胀,钎料基体对体积膨胀的抑制作用将使稀土相内部产生巨大的压应力从而加速Sn晶须的生长.
参考文献
[1] | Zeng K;Tu K N .[J].Materials Science and Engineering,2002,38(02):55. |
[2] | Pitt C H;Henning R G .[J].Journal of Applied Physics,1964,35(02):459. |
[3] | Peach M O .[J].Journal of Applied Physics,1952,23(12):1401. |
[4] | Frank F C .[J].Philosophical Magazine,1953,44:854. |
[5] | Eshelby J D .[J].Physiological Reviews,1953,91:755. |
[6] | Amelinck X S;Bontinck W;Dekeyser W et al.[J].Physics Magazine 8th,1957,82(15):355. |
[7] | Kadesch J S;Brusse J A.[A].Helsingor,Denmark,2000:10. |
[8] | Kakeshita T;Kawanaka R;Hasegawa T .[J].Journal of Materials Science,1982,17:2560. |
[9] | Fisher R M;Darken L S;Sand K G .[J].Acta Metallurgica,1954,2(03):368. |
[10] | Hasiguti R R .[J].Acta Metallurgica,1955,3(02):200. |
[11] | Tu K N .[J].Physical Review B,1994,49(03):2030. |
[12] | 郝虎,田君,史耀武,雷永平,夏志东.SnAgCuY系稀土无铅钎料显微组织与性能研究[J].稀有金属材料与工程,2006(z1):121-123. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%