叶黄素敏化介孔TiO2电极的制备及特性

功能材料, 2005, 36(7): 1072-1079.

1.西北工业大学,电流变技术研究所,陕西,西安,710072

2.西北工业大学,电流变技术研究所,陕西,西安,710072

基金项目: 国家自然科学基金(50025207)

Preparation and properties of mesoporous TiO2 electrode sensitized by xanthophyll

通过表面活性剂的蒸发诱导自组装获得高比表面积(166.89m2/g)的介孔TiO2电极材料,将其调制研磨后滚涂在ITO膜导电玻璃上,煅烧后吸附叶黄素实现电极敏化.结果表明,在植物体内不具备光电化学活性的叶黄素,在介孔TiO2膜电极中却表现出活跃的光电化学活性,光电池的开路光电压达594mV.

[1]	Bach U.;Lupo D.;Comte P.;Moser JE.;Weissortel F.;Salbeck J. .Solid-state dye-sensitized mesoporous TiO2 solar cells with highphoton-to-electron conversion efficiencies[J].Nature,1998(6702):583-585.
[2]	O'Regan B;Gratzel M.[J].NATURE,1991:737-739.
[3]	戴松元;王孔嘉.[J].太阳能学报,1996:220-224.
[4]	Grosso D.;Babonneau F.;Sanchez C.;Albouy PA. Brunet-Bruneau A.;Balkenende AR.;Soler-Illia GJDAA. .Highly organized mesoporous titania thin films showing mono-oriented 2D hexagonal channels[J].Advanced Materials,2001(14):1085-0.
[5]	Smestad GP.;Gratzel M. .Demonstrating electron transfer and nanotechnology: A natural dye-sensitised nanocrystalline energy converter[J].Journal of Chemical Education,1998(6):752-756.
[6]	Takagi S.[J].Agricultural and Biological Chemistry:1211-1231.
[7]	Craft N E;Scared J H.[J].Journal of Agricultural and Food Chemistry,1992:431-434.
[8]	Ma T;Kida T.[J].Electrochemistry Communications,2003:369-372.
[9]	Sawada M;Higuchi M .[J].Thin Solid Films,1998,317:157-160.
[10]	朱月秀,王德苗.SnO2膜导电玻璃性能的研究[J].材料科学与工程,2002(01):72-74.
[11]	匡廷云.光合作用原初光能转化过程的原理与调控[M].南京:江苏科学技术出版社,2003

上一张下一张

计量

作者相关

文章评分