分别采用钛酸异丙酯和钛酸丁酯为先驱体,对所制备的单分散氧化硅球(Ф≈400 nm)进行了1次和2次包覆TiO2层,获得了单分散的SiO2-TiO2芯-壳结构的球;采用TEM,SEM和EDS对所得SiO2-TiO2的球的大小、形貌和球中硅、钛含量进行了表征.研究结果表明:采用钛酸异丙酯作为先驱体可获得氧化钛层较薄但无粘结的SiO2-TiO2芯-壳结构的球(φ可达500 nm);而采用钛酸丁酯作为先驱体时,则可获得较厚但粘结的SiO2-TiO2芯-壳结构的球(φ可达600nm).
参考文献
| [1] | 张辉,赵晓峰,唐清,李文超.准完全带隙的光波段二氧化硅光子晶体材料的制备[J].硅酸盐学报,2002(06):735-738. |
| [2] | Xia Y;Gates B;Yin Y;Lu Y .[J].Advanced Materials,2000,12:693-713. |
| [3] | Bardosova M;Tredgold R H .[J].Journal of Materials Chemistry,2002,12(10):2835-2842. |
| [4] | Wijnhoven J;Vos W L .[J].Science,1998,281:802-804. |
| [5] | Harrison MT.;Rogach AL.;Kornowski A.;Eychmuller A.;Weller H.;Kershaw SV. .Wet chemical synthesis of highly luminescent HgTe/CdS core/shell nanocrystals[J].Advanced Materials,2000(2):123-125. |
| [6] | Johnson N P;McComb D W;Richel A et al.[J].Synthetic Metals,2001,116(1-3):469-473. |
| [7] | Holgado M.;Ibisate M.;Serna CJ.;Lopez C.;Meseguer F.;Cintas A. .Three-dimensional arrays formed by monodisperse TiO2 coated on SiO2 spheres[J].Journal of Colloid and Interface Science,2000(1):6-11. |
| [8] | Hsu WP;Yu R;Matijevic E .[J].Journal of Colloid and Interface Science,1993,156(01):56-65. |
| [9] | 李群艳,董鹏,刘忍肖,白元强.单分散SiO2/TiO2/SiO2多层复合微球的制备[J].无机材料学报,2001(05):896-902. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%