利用大气等离子喷涂技术在45钢基体上制备了WC复合涂层,采用Ml-10摩擦磨损试验机研究了涂层在干摩擦条件下摩擦磨损性能.结果表明:涂层比基体耐磨性高很多,未出现硬质相的剥落;涂层具有典型的"软基体加硬质相"耐磨组织结构,Ni包Al粉末的加入强化了软相,涂层在干摩擦条件下表现出来比较优良的耐磨性;由于气孔不可避免存在于涂层,涂层磨痕在气孔处出现断裂和塌陷现象,因此提高涂层致密性能降低涂层磨损率.
参考文献
| [1] | 尹斌,周惠娣,陈建敏,赵晓琴,安宇龙.等离子喷涂纳米WC-12%Co涂层与陶瓷和不锈钢配副时的摩擦磨损性能对比研究[J].摩擦学学报,2008(03):213-218. |
| [2] | D.A.Stewart;P.H.Shipway .Microstructural evolution in thermally sprayed WC-Co coatings: comparison between nanocomposite and conventional starting powders[J].Acta materialia,2000(7):1593-1604. |
| [3] | Wu Yuping;Lin Pinghua;Chu Chenglin .Cavitation erosion characteristics of a Fe-Cr-Si-B-Mn coating fabricated by high velocity oxy-fuel (HVOF) thermal spray[J].Materials Letters,2007(8/9):1867-1872. |
| [4] | 崔颖,林锋,宋希建,于月光,蒋显亮.热喷涂新型WC/Co耐磨涂层材料研究进展[J].有色金属（冶炼部分）,2006(z1):65-67. |
| [5] | 赵民,R.Gadow,A.Killinger,A.Candel-Ruiz.热喷涂参数对喷涂WC-Co合金表面温度的影响[J].沈阳建筑大学学报（自然科学版）,2006(06):1052-1056. |
| [6] | K. Dobler;H. Kreye;R. Schwetzke .Oxidation of stainless steel in the high velocity oxy-fuel process[J].Journal of Thermal Spray Technology,2000(3):407-413. |
| [7] | 赵敏海,刘爱国,郭面焕,刘德建.等离子熔-喷WC-17%Co涂层工艺参数对外观形貌的影响[J].焊接学报,2005(11):39-42. |
| [8] | 郭面焕,刘爱国,赵敏海,曲军章.等离子熔-喷WC-17%Co涂层的组织结构（Ⅰ）[J].焊接学报,2006(05):5-8. |
| [9] | 胡冰,贺子义,陆益军,张京贤,王萍,吴玉萍,林萍华,谢国治.等离子熔覆WC复合厚涂层特性研究[J].陶瓷学报,2007(01):34-38. |
| [10] | 杜令忠,徐滨士,杨华,张伟刚.超音速等离子喷涂12Co-WC涂层在含沙油润滑条件下的摩擦学行为[J].材料保护,2007(10):65-67. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%