采用溶液相转化法制备了羽绒粉体/聚偏氟乙烯（PVDF）和苎麻粉体/PVDF复合微孔膜,对膜结构和性能进行了分析和测试。结果显示苎麻粉体/PVDF复合膜、羽绒粉体/PVDF复合膜、纯PVDF膜的形态一致,均为致密皮层和多孔亚层,孔隙率和水通量依次降低,结晶度依次增加;但膜的吸水率按照羽绒粉体/PVDF复合膜、苎麻粉体/PVDF复合膜、纯PVDF膜依次下降;这说明复合膜水通量主要受孔隙率的影响,而膜吸水率主要受纤维粉体吸水性大小的影响。膜力学性能测试显示加入粉体之后,PVDF膜的强度增加,断裂伸长率有所下降。
Down powder/PVDF composite membrane and ramie powder/PVDF composite membrane were prepared by the solution phase inversion method,and membrane structure and performances were measured.The experimental results revealed that the porosity and water fluxes decreased gradually as the following order of ramie powder/PVDF composite membrane,down powder/PVDF composite membrane and PVDF membrane.While the membrane crystallinity increased according to the above order.These three membranes displayed the same membrane morphology with the dense skin layer and the porous sublayer.But the water-absorbability reduced in sequence of down powder/PVDF composite membrane,ramie powder/PVDF composite membrane and PVDF membrane.These results showed that porosity had a significant influence on membrane water fluxes and membrane water-absorbability was controlled by hydrophilicity of fiber powder.For membrane mechanical properties,fiber powder addition made PVDF membrane strength enhance with the elongation reduction.
参考文献
| [1] | Cha BJ;Yang JM .Preparation of poly(vinylidene fluoride) hollow fiber membranes for microfiltration using modified TIPS process[J].Journal of Membrane Science,2007(1/2):191-198. |
| [2] | Rana D;Matsuura T;Narbaitz RM;Feng C .Development and characterization of novel hydrophilic surface modifying macromolecule for polymeric membranes[J].Journal of Membrane Science,2005(1/2):103-112. |
| [3] | 姜海凤,马玉新,王铎,高从蝔.PVDF/TiO2杂化超滤膜的制备与表征[J].功能材料,2009(04):591-594. |
| [4] | 郝保红,杨金生,桑福平.超细纳米技术的研究进展和应用前景[J].北京石油化工学院学报,2001(01):44-47. |
| [5] | 梅硕,肖长发,胡晓宇,梁海先.二氧化硅填充聚氯乙烯杂化膜研究[J].功能材料,2009(05):806-808,812. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%