CeO2-Co3O4 catalysts for low-temperature CO oxidation were prepared by a co-precipitation method.In combination with the characterization methods of N2 adsorption/desorption, XRD, temperature-programmed reduction (TPR), and FT-IR, the influence of the cerium content on the catalytic performance of CeO2-Co3O4 was investigated.The results indicate that the prepared CeO2-Co3O4 catalysts exhibit a better activity than that of pure CeO2 or pure Co3O4.The catalyst with the Ce/Co atomic ratio 1:16 exhibits the best activity, which converts 77% of CO at room temperature and completely oxidizes CO at 45 ℃.
参考文献
| [1] | P. Thormahlen;M. Skoglundh;E. Fridell;B. Andersson .Low-Temperature CO Oxidation over Platinum and Cobalt Oxide Catalysts[J].Journal of Catalysis,1999(2):300-310. |
| [2] | Garin F;Simonot L;Maire G .A comparative study of LaCoO3,Co3O4 and LaCoO3-Co3O4.I.Preparation,characterization and catalytic properties for the oxidation of CO[J].Applied Catalysis B:Environmental,1997,11(02):167. |
| [3] | Lahaye J;Boehm S;Chambrion Ph et al.Influence of cerium oxide on the formation and oxidation of soot[J].Combustion and Flame,1996,104(1-2):199. |
| [4] | Liu Wei;Flytzani Stephanopoulos Maria .Total oxidation of carbon monoxide and methane over transition metal fluorite oxide composite catalysts:II.catalyst characterization and reaction-kinetics[J].Journal of Catalysis,1995,153(02):317. |
| [5] | Bernal S.;Cauqui MA.;Cifredo GA.;Pintado JM. Rodriguez-Izquierdo JM.;Blanco G. .Influence of reduction treatment on the structural and redox behaviour of ceria, La/Ce and Y/Ce mixed oxides[J].Catalysis Letters,1998(1/2):51-57. |
| [6] | Cho B K .Chemical modification of catalyst support for enhancement of transient catalytic activity:nitric oxide reduction by carbon monoxide over rhodium[J].Journal of Catalysis,1991,134(01):74. |
| [7] | Rossignol S;Madier Y;Duprez D .Preparation of zirconia-ceria materials by soft chemistry[J].Catalysis Today,1999,50(02):261. |
| [8] | 李梅,柳召刚,胡艳宏,刘铃声,熊晓柏,邱巨峰.Preparation and Characterization of CeO2 Superfine Powder[J].稀土学报(英文版),2003(06):654-656. |
| [9] | Lamonier C;Ponchel A;D′Huysser A et al.Studies of the cerium-metal-oxygen-hydrogen system (metal=Cu,Ni)[J].Catalysis Today,1999,50(02):247. |
| [10] | Villain S;Caban J;Knauth P .Solid state electrochemical characterisation of nanostructured silver prepared by cold-rolling and internal oxidation[J].Scripta Materialia,1998,38(06):1003. |
| [11] | Jiang Y.;Wu Y.;Xie B.;Xie Y.;Qian YT. .Moderate temperature synthesis of nanocrystalline Co3O4 via gel hydrothermal oxidation[J].Materials Chemistry and Physics,2002(2):234-237. |
| [12] | 蒋晓原,周仁贤,袁骏,吕光烈,郑小明.Catalytic Oxidative Properties and Characterization of CuO/CeO2 Catalysts[J].稀土学报(英文版),2003(01):55-59. |
| [13] | Bordiga S;Platero E E;Are(a)n C O et al.Low temperature CO adsorption on Na-ZSM-5 zeolites:An FTIR investigation[J].Journal of Catalysis,1992,137(01):179. |
| [14] | Daniells S T;Overweg A R;Makkee M et al.The mechanism of low-temperature CO oxidation with Au/Fe2O3 catalysts:a combined Mssbauer,FT-IR,and TAP reactor study[J].Journal of Catalysis,2005,230(01):52. |
| [15] | Haruta M;Tsubota S;Kobayashi T et al.Low-temperature oxidation of CO over gold supported on TiO2,α-Fe2O3,and Co3O4[J].Journal of Catalysis,1993,144(01):175. |
| [16] | Ji L.;Lin J. .Metal-Support Interactions in Co/Al_2O_3 Catalysts: A Comparative Study on Reactivity of Support[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2000(8):1783-1790. |
| [17] | Busca G;Lorenzelli V;Escribano V S et al.FT-113 study of the surface properties of the spinels NiAl2O4 and CoAl2O4 in relation to those of transitional aluminas[J].Journal of Catalysis,1991,131(01):167. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%