建立了纳米结构组织锆-4合金腐蚀速率.晶粒尺寸关系模型,计算了高温下纳米组织锆-4合金和腐蚀速率曲线,并与纳米组织锆-4合金在400℃水蒸气中的腐蚀试验数据进行了对比.结果表明:与普通晶粒相比,纳米晶粒尺寸下锆合金的速率低于普通晶粒锆-4合金的腐蚀速率,随着纳米晶粒尺寸的减小,锆-4合金的腐蚀速率也降低;同时,纳米化组织处理推迟了锆-4合金氧化转折时间,使其抗氧化性能得到了提高.
参考文献
| [1] | Comsmck R J;Schoenberg G;Sable G P.[A].Philadelphia:ASTM,1996:710. |
| [2] | Liu J Z;Tian Z Y .[J].Rare Metal Materlals and Engineering,2001,30(z1):1. |
| [3] | Li Z K;Zhou L;Liu J Z et al.[J].Rare Metal Materlals and Engineering,2001,30(z1):52. |
| [4] | Park JY;Kim HG;Jeong YH;Jung YH .Crystal structure and grain size of Zr oxide characterized by synchrotron radiation microdiffraction[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2004(3):433-442. |
| [5] | Xu J;Bai X D;He F et al.[J].Journal of Nuclear Materials,1999,265:240. |
| [6] | 张喜燕,李聪,刘年富,张强,石明华,邱绍宇.纳米结构锆合金组织氧化膜结构演变的XRD分析[J].核动力工程,2007(06):71-75. |
| [7] | Zhang X Y;Shi M H;Li C et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,448(1-2):259. |
| [8] | 江全元,何俊佳,邹积岩,程礼椿.CuCr复合材料的导电性[J].华中理工大学学报,1999(08):78-80. |
| [9] | 黄锡文.[J].电工合金,1998(03):26. |
| [10] | 王从曾.材料性能学[M].Beijing:Beijng University ofTechnology Press,2001:189. |
| [11] | 叶长江;李铁藩;周江龙 .[J].金属学报,1995,31:B109. |
| [12] | 周邦新;李聪 et al.[J].核动力工程,1993,14(02):149. |
| [13] | Jeong Y H;Kim H G;Kim D J et al.[J].Journal of Nuclear Materials,2003,317:73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%