以工业生产的Ti-IF钢热轧板为研究材料,结合连续热镀锌线的工艺特点,采用实验室冷轧、盐浴退火方法和金相、X射线织构测试等分析手段,研究了冷轧压下率对组织和织构的影响规律.试验结果表明,随着冷轧压下率从60%提高到90%,冷轧态α取向线上的取向密度不断增强,而且主要形成了{223}＜110＞和{114}＜110＞织构,γ线上的{111}＜110＞和{111}＜112＞织构亦有所增强;退火后铁素体晶粒尺寸从9.0级细化到10.5级;试验钢退火后仍具有较强的{223}＜110＞和{114}＜110＞织构,且随着冷轧压下率的提高,{111}织构有增强的趋势.要获得强的{111}织构,冷轧压下率需在80%以上.
参考文献
| [1] | Dirk VANDERSCHUEREN;Naoki YOSHINAGA;Kazuo KOYAMA .Recrystallisation of Ti IF Steel Investigated with Electron Backscattering Pattern (EBSP)[J].ISIJ International,1996(8):1046-1054. |
| [2] | Bevis Hutchinson;Dorota Artymowicz .Mechanisms and modeling of microstructure/texture evolution in interstitial-free steel sheets[J].ISIJ International,2001,41(02):404-413. |
| [3] | Hoile S.; .Processing and properties of mild interstitial free steels[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2000(10):1079-1093. |
| [4] | 郑之旺,陈杰,周丹.卷取温度对Ti-IF钢退火过程中组织和织构演变的影响[J].钢铁钒钛,2007(01):1-8. |
| [5] | K.Eloot .Texture Evolution during Cold Rolling and Recrystallisation of IF Steel with a Strong {111} Hot Band Texture[J].ISIJ International,1998(6):602-609. |
| [6] | 郑之旺,陈杰,周丹.卷取温度对Ti-IF钢热轧卷组织和性能的影响[J].钢铁钒钛,2006(04):21-24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%