采用自制半固态搅拌装置研究了Sn-15Pb(质量分数,%下同)合金在搅拌条件下固相分数大于0.6时的连续冷却凝固行为.组织分析结果表明:当搅拌停止温度在合金固相线温度附近时,所获半固态组织出现非常明显的液固两相分离现象,且所获固相组织为分散的类球状颗粒.利用此现象,获得了一种新型金属合金粉末制备方法-半固态金属合金粉末制备法.采用该方法可以实现粉末颗粒内部无夹杂、无孔洞,外部裹有低熔点共晶薄膜.颗粒为以单晶方式生长的金属合金粉末.
参考文献
| [1] | Young K P.[A].Tokyo:Tokyo Institute of Industrial Science,1994:155. |
| [2] | Young K P.[A].Turin:Edimet Spa,2000:97. |
| [3] | Fan Z .[J].International Migration Review,2002,47(02):49. |
| [4] | Garat M.[A].Turin:Edimet Spa,2000:187. |
| [5] | Flemings M C.Science and Technology of Semi-Solid Metal Processing[M].Rosemont:North American Die Casting Association,2001:1. |
| [6] | Flemings M C .[J].Metallurgical Transactions,1991,22A:957. |
| [7] | Kirkwood D H .[J].International Migration Review,1994,39(05):173. |
| [8] | Molenaar J M M et al.[J].Journal of Materials Science,1989,21:389. |
| [9] | Ohtani H et al.[J].JPhase Equilibria,1995,16:416. |
| [10] | Young K P.[A].Sheffield:University of Sheffield and the Metal Society,1977:510. |
| [11] | Lehuy H et al.[J].Journal of Materials Science,1985,20:105. |
| [12] | 张世江 .Zn-Al合金的搅动凝固特性及其铸态组织与拉伸性能[D].东南大学,1993. |
| [13] | 李涛,黄卫东,林鑫.半固态处理中球晶形成与演化的直接观察[J].中国有色金属学报,2000(05):635. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%