运用正交试验方法研究以羧甲基纤维素钠(CMC)和硅灰按不同比例配制的分散体系对碳纤维在水泥浆体中分散性的影响,采用新拌料浆法从多份新拌的水泥浆料中分离出碳纤维,并计算碳纤维质量的变动系数,由变动系数评价碳纤维的分散性和分散剂的作用效果.在各种CMC掺量下,硅灰均能显著改善碳纤维的分散性.随着CMC掺量的增加,碳纤维分散性提高.当CMC掺量为0.8%,硅灰掺量为15%时,CMC和硅灰的共同作用使变动系数最小,此时碳纤维在水泥基体中分散性最好,为最佳的分散剂配比.
参考文献
| [1] | Pu-Woei Chen;D D L Chung.Carbon fiber reinforced concrete for smart structures capable of non-destructive flow detection[J].Smart Materials and Structures,1993(02):22-30. |
| [2] | 毛起炤;杨元霞;沈大荣 等.碳纤维增强水泥压敏性影响因素的研究[J].硅酸盐学报,1997,25(06):734-737. |
| [3] | Mingqing Sun;Zhuoqiu Li;Qingping Liu .the electromechanical effect of carbon fiber reinforced cement[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(12):2273-2275. |
| [4] | Weiming Lu;Xuli Fu;D D L Chung .A comparative study of the wettability of steel, carbon and polyethylene fibers by water[J].Cement and Concrete Research,1998,28(06):783-786. |
| [5] | 关新春,韩宝国,欧进萍.碳纤维在水泥浆体中的分散性研究[J].混凝土与水泥制品,2002(02):34-36. |
| [6] | Xuli Fu;D D L Chung .Effect of methylcellulose admixture on the mechanical properties of cement[J].Cement and Concrete Research,1996,26(04):535-538. |
| [7] | 杨元霞,毛起炤,沈大荣,李卓球.碳纤维水泥基复合材料中纤维分散性的研究[J].建筑材料学报,2001(01):84-88. |
| [8] | 候作富,李卓球,胡胜良.硅灰对碳纤维导电混凝土电阻率和强度的影响[J].混凝土,2003(02):26-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%