采用纳米AIN作为导热填料,经硅烷偶联剂KH-570表面改性后与环氧树脂(EP)共混制备了导热绝缘胶.通过红外光谱(FT-IR)、接触角方法对改性后纳米AIN进行分析和表征,结果表明,KH-570成功包覆到了纳米AIN表面,粉体由亲水性变为疏水性;对于纳米AIN/EP导热绝缘胶,随着改性纳米AIN填充量的增加,导热率呈上升趋势;当KH-570用量为3.5%、纳米AIN量为20%时,导热率达到0.632W/(m·K),是纯环氧树脂胶的3倍多;此时体积电阻率为2.6×1013Ω·cm,剪切冲击强度为11.9×1015J/m2.
参考文献
| [1] | 张晓辉;徐传骧 .[J].电力电子技术,1999,5:61-62. |
| [2] | Wang JJ.;Yi XS. .Preparation and the properties of PMR-type polyimide composites with aluminum nitride[J].Journal of Applied Polymer Science,2003(14):3913-3917. |
| [3] | Xu Y S;Chung D D;Cathleen M .[J].Composites PartA,2001,32:1749-1757. |
| [4] | 王政.用于集成电路封装的有机复合高导热灌封料[J].安徽化工,2001(01):41-44. |
| [5] | 毋伟;陈建峰;卢寿慈.超细粉体表面修饰[M].北京:化学工业出版社,2004 |
| [6] | Lee G W;Park M;Kim J et al.[J].Composites Part A:Applied Science and Manufacturing,2006,37:1345-1350. |
| [7] | Lee ES;Lee SM;Cannon WR;Shanefield DJ .Improved dispersion of aluminum nitride particles in epoxy resin by adsorption of two-layer surfactants[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2008(1/3):95-103. |
| [8] | 过梅丽.高聚物与复合材料的动态力学热分析[M].北京:化学工业出版社,2002 |
| [9] | 马传国,容敏智,章明秋.导热高分子复合材料的研究与应用[J].材料工程,2002(07):40-45. |
| [10] | 陈祥宝 .[J].复合材料学报,1996,13(04):1-7. |
| [11] | 张猛,高彦芳,阜巍,江宇,周其庠,刘德山.液晶聚酯/氮化铝复合基板材料制备中偶联剂的应用[J].复合材料学报,1998(03):71-74. |
| [12] | 才庆魁,贺春林,赵明久,毕敬,刘常升.亚微米级SiC颗粒增强铝基复合材料的拉伸性能与强化机制[J].金属学报,2003(08):865-869. |
| [13] | Lange F F;Radford K C .[J].Journal of Materials Science,1979,6:1197-1203. |
| [14] | Bhattacharya S K.Metal-filled Polymers Properties and Applications[M].New York,USA:Marcel Dekker,Inc,1986 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%