以1%(质量分数,下同)蜘蛛丝和9%聚-L-乳酸(PLLA)的混合液为纺丝溶液,采用静电纺丝方法制备了蜘蛛丝/PLLA复合纤维构成的连续纱线.探讨了纺丝温度、卷绕速度、后拉伸倍数等对纤维和纱线的形态结构及力学性能的影响.研究发现,加入蜘蛛丝蛋白后,PLLA复合纱线的强度提高了13%,纤维直径从1.1 μm减小到了550 nm;加热区温度为150℃时纱线强度最大;卷绕速度为(105±5)r/min时可以实现稳定纺丝;拉伸1.5倍时,纱线断裂强度和初始模量分别提高了66%和92%,断裂伸长率下降.
参考文献
| [1] | Ana C. Macintosh;Victoria R. Kearns;Aileen Crawford .Skeletal tissue engineering using silk biomaterials[J].Journal of tissue engineering and regenerative medicine,2008(2/3):71-80. |
| [2] | Seidel A.;Jelinski LW.;Liivak O. .Artificial spinning of spider silk[J].Macromolecules,1998(19):6733-6736. |
| [3] | Shahrzad Zarkoob;R.K.Eby;Darrell H.Reneker;Steven D.Hudson;Dale Ertley;Wade W.Adams .Structure and morphology of electrospun silk nanofibers[J].Polymer: The International Journal for the Science and Technology of Polymers,2004(11):3973-3977. |
| [4] | 许箐 .再生蜘蛛丝的成丝方法及其结构与性能[D].苏州大学,2005. |
| [5] | 张长胜,潘志娟,夏艳杰,许箐.纳米再生蜘蛛包卵丝的纺制及其结构与性能[J].丝绸,2006(01):16-19. |
| [6] | Chin-San Wu;Hsin-Tzu Liao .A new biodegradable blends prepared from polylactide and hyaluronic acid[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(23):10017-10026. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%