目前,制备碳纳米管的方法甚多,碳氢化合物催化裂解法是最有希望实现大规模生产的合成方法.该方法中催化剂的选择又是成功制备碳纳米管的关键,因此对当前使用的各种催化剂进行了分类讨论和总结.
参考文献
| [1] | Iijimas .Helical Microtubules of Griphitic Carbon[J].Nature,1991,354:56. |
| [2] | Chen P.;Lin GD.;Hong Q.;Tsai KR.;Zhang HB. .GROWTH OF CARBON NANOTUBES BY CATALYTIC DECOMPOSITION OF CH4 OR CO ON A NI-MGO CATALYST[J].Carbon: An International Journal Sponsored by the American Carbon Society,1997(10/11):1495-1501. |
| [3] | ChenXH;Chen C S;Chen Q et al.Non-destructive purification of multi-walled carbon nanotubes produced by catalyzed CVD[J].Materials Letters,2002,57:734. |
| [4] | 王健雄,陈小华,彭景翠,张振华.碳纳米管的非破坏性纯化研究[J].新型炭材料,2001(03):37-41. |
| [5] | 林敬东,杨乐夫,蔡云,王欣莹,陈鸿博,张鸿斌,廖代伟.多壁碳纳米管的纯化[J].厦门大学学报(自然科学版),2001(04):888-892. |
| [6] | Li H.;Gao LZ.;Tang SH.;Cheng ZY.;Zhang BL.;Yu ZL.;Ng CF. Au CT.;Liang Q. .Catalytic production of carbon nanotubes by decomposition of CH4 over the pre-reduced catalysts LaNiO3, La4Ni3O10, La3Ni2O7 and La2NiO4[J].Catalysis Letters,2001(3/4):185-188. |
| [7] | Liu BC.;Tang SH.;Yu ZL.;Zhang BL.;Chen T.;Zhang SY. .Catalytic growth of single-walled carbon nanotubes with a narrow distribution of diameters over Fe nanoparticles prepared in situ by the reduction of LaFeO3[J].Chemical Physics Letters,2002(3-4):297-300. |
| [8] | AlvarezWE;Kitiyanan B;Borgna A et al.Synergism of Co and Mo in the catalytic production of single-wall carbon nanotubes by decomposition of CO[J].Carbon,2001,39:547. |
| [9] | HernadiK;Fonseca A;Nagy J B et al.Catalytic synthesis of carbon nanotubes using zeolite support[J].Zeolites,1996,17:416. |
| [10] | Benito AM.;Munoz E.;Martinez MT.;Maniette Y. .Carbon nanotubes production by catalytic pyrolysis of benzene[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(5/6):681-683. |
| [11] | Huczko A. .Synthesis of aligned carbon nanotubes [Review][J].Applied physics, A. Materials science & processing,2002(5):617-638. |
| [12] | Sun H.D.;Chen J.;Li G.;Tang Z.K. .Synthesis and Raman characterization of mono-sized single-wall carbon nanotubes in one-dimensional channels of AlPO_4-5 crystals[J].Applied physics, A. Materials science & processing,1999(4):381-384. |
| [13] | LiWZ;Xie S S;Qian L X et al.Large-scale synthesis of aligned carbon nanotubes[J].Science,1996,274:1701. |
| [14] | 王振霖,王太宏.基于阳极氧化法的纳米结构加工和纳米器件的制备[J].微电子技术,2001(05):17-21. |
| [15] | Wenchong Hu;Dawei Gong;Zhi Chen;Liming Yuan;Kozo Saito;Craig A. Grimes;Padmakar Kichambare .Growth of well-aligned carbon nanotube arrays on silicon substrates using porous alumina film as a nanotemplate[J].Applied physics letters,2001(19):3083-3085. |
| [16] | Soo-Hwan Jeong;Hee-Young Hwang;Kun-Hong Lee;Yongsoo Jeong .Template-based carbon nanotubes and their application to a field emitter[J].Applied physics letters,2001(14):2052-2054. |
| [17] | Z. H. Yuan;H. Huang;H. Y. Dang;J. E. Cao;B. H. Hu;S. S. Fan .Field emission property of highly ordered monodispersed carbon nanotube arrays[J].Applied physics letters,2001(20):3127-3129. |
| [18] | JongWJ;Lai S H;Hong K H .The effect of catalysis on the formation of one-dimensional carbon structured materials[Z]. |
| [19] | RenZF;Huang Z P;Xu J W et al.Synthesis of large arrays of wall-aligned carbon nanotubes on glass[J].Science,282:1105. |
| [20] | HuangZP;Wang D Z;Wen J G et al.Effect of nickel,iron and cobalt on growth of aligned carbon nanotubes[J].Applied Physics A:Materials Science and Processing,2002,74:387. |
| [21] | Qin LC.;Krauss AR.;Gruen DM.;Zhou D. .Growing carbon nanotubes by microwave plasma-enhanced chemical vapor deposition[J].Applied physics letters,1998(26):3437-3439. |
| [22] | SohnJI;Lee S .Micropatterned vertically aligned carbonnanotubes growth on a Si surface or inside trenches[J].Applied Physics A:Materials Science and Processing,2002,74:287. |
| [23] | ZhangWD;Wen Y;Tjiu W C et al.Growth of vertically aligned carbon nanotubes array on large area of quartz plates by chemical vapor deposition[J].Applied Physics A:Materials Science and Processing,2002,74:419. |
| [24] | CaoA;Ci L;Li D et al.[J].Chemical Physics Letters,2001,335:150. |
| [25] | Cheng HM.;Su G.;Pan HY.;He LL.;Sun X.;Dresselhaus MS.;Li F. .Large-scale and low-cost synthesis of single-walled carbon nanotubes by the catalytic pyrolysis of hydrocarbons[J].Applied physics letters,1998(25):3282-3284. |
| [26] | Li F.;Xing YT.;Tan PH.;Su G.;Cheng HM. .Purification of single-walled carbon nanotubes synthesized by the catalytic decomposition of hydrocarbons[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(14):2041-2045. |
| [27] | CaoA;Zhang X;Xu C et al.Thinning and diluting aligned carbon nanotube films for uniform field emission[J].Applied Physics A:Materials Science and Processing,2002,74:415. |
| [28] | Elizabeth C. Dickey;Craig A. Grimes;Mahaveer K. Jain;Keat G. Ong;Dali Qian;P. D. Kichambare;Rodney Andrews;David Jacques .Visible photoluminescence from ruthenium-doped multiwall carbon nanotubes[J].Applied physics letters,2001(24):4022-4024. |
| [29] | Gallium-mediated growth of multiwall carbon nanotubes[J].Applied physics letters,2003(12):1947-1949. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%