对热型连铸锌铝合金定向凝固线材的铸态及热处理组织进行了观察、 分析和讨论。 结果表明: 热型连铸锌铝合金线材的显微组织为定向生长的平行柱状枝晶组织; 共晶合金ZA5的枝状共晶的每个枝晶都由多层片状共晶β和η两相构成, 过共晶合金的组织为初生树枝晶和枝晶间共晶组织, 其中ZA8, ZA12初生相为β相, ZA22和ZA27的初生相是α相。

The as-cast and heat treatment microstructure of ZA alloy rod directionally solidified by continuous casting has been analyzed. The results show that the microstructure of the ZA alloy lines is the parallel directional dendritic columnar crystal. Every dendritic crystal of eutectic alloy ZA5 is composed of many layer eutectic β and η phases. The microstructure of hyper eutectic ZA alloys is primary dendritic crystal and interdendritic eutectic structure. The primary phase of ZA8 and ZA12 is β phase, but the primary phase of ZA22 and ZA27 is α phase.

参考文献

[1] Ohno A.Continuous casting of single crystal ingots by the OCC process[J].Journal of Metals,1986(38):14-16.
[2] Ohno A;Motoyasu G.Solidification Process[A].London:The Institute of Metals,1988
[3] SODA H;Motoyasu G;Mclean A.Alloy casting by the horizontal Ohno continuous casting system[J].Cast Metals,1993(02):76-86.
[4] 郝远,陈体军,寇生中.SiCp含量及粒度对锌基复合材料高温摩擦磨损性能的影响[J].中国有色金属学报,1997(03):132-136.
[5] Rutter J W;Chalmers B .Asprismatic substructure formed during solidification of metals[J].Canadian Journal of Physics,1953,31:15-39.
[6] Tiller W A;Jackson K A;Rutter J W .The redistribution of solute atoms during the solidification of metals[J].Acta Materialia,1953,1(01):428-437.
[7] 胡秀莲,李世春.Zn-5Al合金铸态共晶结构的研究[J].材料工程,1997(11):20.
[8] Gervais E;Levert H;Bess M .The development of a family of zinc-based foundry alloys[J].AFS Transactions,1980,88:183-194.
[9] Pollard W A .Assessment of the sand-casting properties of zinc-base foundry alloys A2430 (AC121)[R].Mines Branch Investigation Report IR 64-51. Ottawa: Canadian Metallurgical Society,1964.
[10] Sahoo M;Whiting L V;Chartrand V et al.Effect of strontium on the structure and mechanical properties of Zn-Al foundry alloys[J].AFS Transactions,1986,44:225-242.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%