This paper presents an investigation on the primary microstructure and mechanical properties of a martensite-austenitic duplex steel precipitation-hardened by VC carbide. The results show that the mechanical properties at room temperature are strongly dependent upon the volume fraction of austenite fA. When fA < 32 % both ultimate strength and Vield strength are decreased with increasing fA. however. whenfA>32%, with increasing the.fA. ultimate strength rises and yield strength drops down. Experimental results at elevated temperatures. show that when test temperature ≤500℃. the yield strength to modulus ratio remains unchanged, however. as the temperature rises a substantial fall in the ratio occurs. The strength values at 600 and 700℃ are increased with increasing strain rate measured by cross-head speed of testing rnachine, The law of mixtures and the contribution of strain-induced transformation from unstable austen ite to martensite to the mechanical properties are discussed.

参考文献

[1]
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%