研究了氧化铝陶瓷分别在800℃、1000℃和1200℃热处理后的耐盐酸腐蚀性.结果表明:实验过程中样品的晶相稳定,不会出现第二相,且热处理对氧化铝陶瓷的耐盐酸腐蚀性有改善作用.较高温度热处理能够改变样品的气孔率等,改善样品的致密度,从而在盐酸腐蚀过程中使样品与盐酸的反应减缓,提高样品的耐盐酸腐蚀性.
参考文献
| [1] | WOO LEE;RAN Jl;ULRICH GOSELE .Fast fabrication of long-range ordered porous alumina membranes by hard anodization[J].Nature materials,2006(9):741-747. |
| [2] | Yunyang Liu;Zhenfu Ng;Easir A. Khan .Synthesis of continuous MOF-5 membranes on porous α-alumina substrates[J].Microporous and Mesoporous Materials,2009(1/3):296-301. |
| [3] | Kiyoharu Tadanaga;Noriko Katata;Tsutomu Minami .Super-water-repellent Al_2O_3 coating films with high transparency[J].Journal of the American Ceramic Society,1997(4):1040-1042. |
| [4] | 赵斌,饶保林.聚酰亚胺/纳米氧化铝复合薄膜的研究[J].绝缘材料,2005(06):23-25,29. |
| [5] | 范勇,安军伟,周宏,刘伟.纳米氧化铝杂化聚酰亚胺薄膜的制备与性能研究[J].绝缘材料,2007(02):1-3,6. |
| [6] | 王伟,刘立柱,杨阳,雷清泉.聚酰亚胺/氧化硅/氧化铝纳米杂化薄膜的制备及结构与性能研究[J].绝缘材料,2005(05):11-14. |
| [7] | 雷杨俊,肖定全.真空中氧化铝陶瓷表面耐压试验研究[J].绝缘材料,2004(03):29-31,35. |
| [8] | Surface morphology control on porous anodic alumina in phosphoric acid[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2010(14):p.3797. |
| [9] | Bu J L;Wang P C;Ai L Q et al.Study on Erosion-Abra-sion Properties of Al-Mn Alloy and Its Composite Rein-forced with Al2O3 Particulates[J].Advances in Materials Research,2011,287-290:599-602. |
| [10] | 张磊,董应超,杨家奎,刘杏芹,孟广耀.堇青石和氧化铝支撑体的耐腐蚀研究[J].膜科学与技术,2009(02):22-27. |
| [11] | 孔德顺,蒋荣立,陈文龙,张宗祥.煤系高岭土二次煅烧水热合成P型分子筛[J].化工矿物与加工,2007(06):23-25,35. |
| [12] | 周健儿,赵世凯,胡学兵,汪永清,王德林.预烧温度对二次煅烧工艺合成的针状莫来石显微形貌的影响[J].人工晶体学报,2010(05):1281-1285. |
| [13] | 付鹏,刘卫东,吴细桂.氧化铝陶瓷生产工艺中的质量控制[J].佛山陶瓷,2005(05):24-27. |
| [14] | 王零森.特种陶瓷[M].长沙:中南大学出版社,2005 |
| [15] | 刘大成 .Al2O3陶瓷及其烧结[J].中国陶瓷,1998,34(05):13-15. |
| [16] | 吴振东,叶建东.添加剂对氧化铝陶瓷的烧结和显微结构的影响[J].兵器材料科学与工程,2002(01):68-72. |
| [17] | 刘勇,陈晓银.氧化铝热稳定性的研究进展[J].化学通报,2001(02):65-70. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%