研究了以三嵌段共聚物P123为模板剂，氯化铁或过硫酸铵作为氧化剂时，纳米结构聚吡咯的制备和形貌调控的方法，发现加入P123作为模板剂可得到球状的纳米聚吡咯，而无P123存在时产物是形状不规则的纳米颗粒。P123的浓度和氧化剂的种类均会显著地影响聚吡咯的粒径和电导率。在相同的氧化剂条件下，随着P123浓度的升高，聚吡咯的平均粒径变小。P123的加入使得聚吡咯的电导率显著提高。无论是否存在模板剂调控，氯化铁作为氧化剂得到的产物的电导率比过硫酸铵作为氧化剂得到产物的电导率大。
Synthesis and morphology control of nano-polypyrrole were studied, when P123, a kind of triblock copolymers, was used as a template agent, and ferric chloride or ammonium persulfate acted as oxidant. Spherical PPy nanoparticles were obtained when Pi23 was present, while irregular nanoparticles were gotten when P123 was absent. Both the concentration of P123 and the kind of oxidant could influence the diameter of PPy particles and the electrical conductivity of PPy. The average diameter of PPy particles decreased as the concentration of P123 increased when the same oxidant was used. The electrical conductivity of PPy was obviously increased by the presence of Pt23 in synthesis. Whether P123 was presence or not, the electrical conductivity of PPy acquired in reaction in which ferric chloride acted as the oxidant was notably higher than that of PPy acquired when ammonium persulfate acted as the oxidant .
参考文献
| [1] | Wu QF;He KX;Mi HY;Zhang XG .Electrochemical capacitance of polypyrrole nanowire prepared by using cetyltrimethylammonium bromide (CTAB) as soft template[J].Materials Chemistry and Physics,2007(2/3):367-371. |
| [2] | Shuangxi Xing;Guoku Zhao .Morphology and thermostability of polypyrrole prepared from SDBS aqueous solution[J].Polymer bulletin,2006(6):933-943. |
| [3] | 李倩倩,黄健涵,刘素琴,关鲁雄,黄可龙.对甲苯磺酸掺杂聚吡咯的合成、表征及其对金属镁的防腐蚀性能研究[J].化学学报,2008(05):571-575. |
| [4] | Jyongsik Jang;Hyeonseok Yoon .Facile fabrication of polypyrrole nanotubes using reverse microemulsion polymerization[J].Chemical communications,2003(6):720-721. |
| [5] | Sargin PS.;Yurtsever E.;Toppare L. .GROWTH MECHANISMS OF POLYPYRROLES[J].Polymer: The International Journal for the Science and Technology of Polymers,1996(7):1151-1155. |
| [6] | 葛东涛 .高分子诱导法电化学制备聚吡咯纳米线[D].天津大学,2003. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%