使用羟基酸类单体对端羧基聚酯预聚物进行封端获得的水溶性聚酯树脂,具有30 mgKOH/g~60mgKOH/g的酸值范围与20mgKOH/g~130mgKOH/g的羟值范围,-50℃~60℃的玻璃化温度,3000~13000的数均分子量.该树脂具有良好的水溶性、储存稳定性、抗水解性、耐水性以及优秀的涂膜性能等,适用于涂料、油墨、粘合剂、及化纤纺织等领域.
A water-soluble polyester resin made by using hydroxy acid monomers end-capping the carboxyl-ter-minated polyester prepolymer,includes an acid value range of 30mgKOH/g ~60mgKOH/g and a hydroxyl value scope of 20mgKOH/g~130mgKOH/g,with a glass transition temperature range from -50℃ to 60℃ and a number average molecular weight of 3000~13000. This resin has excellent water solubility,storage stability,hydrolysis re-sistance,water resistance and outstanding mechanical properties,it is suitable for coating,ink,adhesive,textile and chemical fiber etc.
参考文献
| [1] | 程万里;涂伟萍.水性聚酯的合成及性能研究进展[J].热固性树脂,2009(2):56-59. |
| [2] | 岳慧艳.水性聚酯树脂的研制[J].涂料工业,2003(09):10-11. |
| [3] | 欧阳鎏;王炼石;张安强;阮伟明;冯兆均;冯兆华.自乳化聚酯树脂汽车中涂漆的合成及性能研究[J].热固性树脂,2008(4):25-29. |
| [4] | 王纲;严业崧;张军;刘新泰.聚酯水分散体的合成研究[J].中国涂料,2004(10):20-23. |
| [5] | 王承伟.水性聚酯卷材涂料的研制与开发[J].上海涂料,2009(02):5-6. |
| [6] | 俞剑峰;潘红霞;周晓东.水性卷材涂料用聚酯树脂的制备及涂层性能研究[J].涂料工业,2013(8):42-46. |
| [7] | 闫福安.水性聚酯树脂的合成研究[J].涂料工业,2003(03):9-12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%