采用双辊薄带铸轧机制备出磷含量(质量分数,%)为0.15%的新型高磷耐候钢薄带.对比研究了常规薄带和铸轧薄带冷轧退火后的组织、深拉伸性能,并通过对常规薄带和铸轧薄带中心层织构演变规律的分析探讨了冷轧退火后的铸轧薄带深拉伸性能较好的原因.结果表明,在设定的工艺条件下冷轧退火后,铸轧薄带和常规薄带的组织均为铁素体和珠光体组成的平衡态组织,铸轧薄带纵断面上晶粒取向分布更均匀;常规薄带和铸轧薄带中γ取向线强度相当,导致塑性应变比(-r)值相当,而铸轧薄带中{111}＜110＞织构强度比常规薄带降低50%导致△r大幅减小,提高了深拉伸性能.
参考文献
| [1] | 林兆森,李娜,邱以清,刘振宇,刘相华,王国栋.双辊铸轧高磷铜钢薄带的偏析行为及对力学性能的影响[J].稀有金属,2006(z2):68-71. |
| [2] | Zhenyu LIU;Zhaosen LIN;Yiqing QIU .Segregation in Twin Roll Strip Cast Steels and the Effect on Mechanical Properties[J].ISIJ International,2007(2):254-258. |
| [3] | LI Na;LIU Zhen-yu;QIU Yi-qing.P and Cu Segregation Behavior in Strip Cast Low C Steels[A].Korea,2006:964. |
| [4] | G.P. Zhou;Z.Y. Liu;Y.Q. Qiu;G.D. Wang .The improvement of weathering resistance by increasing P contents in cast strips of low carbon steels[J].Materials & design,2009(10):4126-4135. |
| [5] | XU Ping-guang;YIN Fu-xin;NAGAI Koto .Solidification Cooling Rate and As-Cast Textures of Low-Carbon Steel Strips[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006,441(1/2):157. |
| [6] | 吕庆功,陈光南,周家琮,唐历.深冲钢板的主要织构对塑性应变比的影响[J].钢铁研究,2000(05):40-43. |
| [7] | Ray K;Jonas J J;Hook R E .Cold Rolling and Annealing Textures in Low Carbon and Extra Low Carbon Steels[J].International Materials Reviews,1994,39(04):129. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%