制备了聚对苯二甲酸乙二醇酯-层状硅酸盐(LS)纳米复合材料(NPET),其分子量高、分布窄、力学性能好且薄膜较透明.选择处理剂分子链长短、控制其与基体之间的强或弱相互作用、控制LS加量与加入方式,可得到稳定高性能的NPET.LS以干态或湿态加入使PET结晶速率提高3倍左右,无机相以平均30 nm～70 nm尺度分散于PET基体,有约3%～4%数量的凝聚粒子与基体相分离,使NPET冲击韧性下降.
参考文献
| [1] | 柯扬船 .中国科学院化学所博士后出站报告[R].,1998. |
| [2] | Sellinger A;Weiss P M;Nguyen A.[J].NATURE,1998:256. |
| [3] | Wang Y;Herron N .[J].Science,1996,273:632. |
| [4] | 漆宗能;柯扬船 .[P].CN 97104055.9,1997. |
| [5] | 漆宗能;柯扬船 .[P].CN1187506A,1998. |
| [6] | 柯扬船 .[P].CN:01131141.8,2001. |
| [7] | Ke Y C;LongC F .[J].Journal of Applied Polymer Science,1999,71:1139. |
| [8] | 漆宗能;李强 等.[P].CN139643 6,1996. |
| [9] | Lan T;Kaviratna P D;Pinnavaia T J .[J].Chemistry of Materials,1995,7:2144. |
| [10] | Giannelis E P .[J].Advanced Materials,1996,8(01):29. |
| [11] | Usuki A et al.[P].U S P 4889885,1989. |
| [12] | Ke YC.;Yang ZB.;Zhu CF. .Investigation of properties, nanostructure, and distribution in controlled polyester polymerization with layered silicate[J].Journal of Applied Polymer Science,2002(13):2677-2691. |
| [13] | Avrami M .[J].Journal of Chemical Physics,1939,7:1103. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%