以赤泥、粉煤灰为主要原料,采用水玻璃作为碱激发剂,制备出一种具有较高早期强度的免烧成矿物聚合物胶凝材料.通过实验初步探讨了碱激发剂对该矿物聚合物强度发展的影响.利用合适配比的赤泥/粉煤灰胶凝材料作为基质原料,用细沙作骨料,制成了一种赤泥/粉煤灰基矿物聚合物免烧材料.当赤泥的加入量在60%~70%范围时,各组试样的3 d抗压强度均在10 MPa以上,符合非承重墙体建筑材料的强度MU10级要求.同时本文还对该矿物聚合物材料中胶凝反应机理进行了初步探讨.
The high early compressive strength geopolymer is prepared by using red-mud and fly ash as the main raw materials, adding suitable water glass as alkali exciting agent. Influence of alkali exciting agent to the development of compressive strength of the samples was discussed in this paper. The non-sintering materials were prepared by using silver sand as the aggregate cementing with red-mud and fly ash geopolymer. When adding amounts of red-mud are between 60%-70%, the compressive strength of all samples in the third day is higher than 10 MPa, they satisfy the demand of MU10 high quality for free-bearing wallboard materials. The mechanism of cementing reaction is also discussed briefly.
参考文献
| [1] | 王恩,倪文,孙汉.工业固体废弃物制备地质聚合物技术的原理与发展[J].矿产综合利用,2005(02):30-34. |
| [2] | 倪文;王恩;周佳 .矿物聚合物-21世纪的绿色胶凝材料[J].产业论坛,2003,6:24-28. |
| [3] | 段宏伟,倪文,李建平.地质聚合物在新型建材中的应用[J].新型建筑材料,2004(01):14-15. |
| [4] | Ko IKEDA,Dang FENG,Akira MIKUNI.地质聚合物技术的发展近况[J].地学前缘,2005(01):206-213. |
| [5] | 杨慧芳;张强.固体废物资源化[M].北京:化学工业出版社,2004:217-223. |
| [6] | 程秀兰 .粉煤灰综合利用现状概述[J].资源与环境,2007,35:147-148. |
| [7] | 于永波,王克勤,王皓,陈津.山西铝厂赤泥性质的研究[J].太原理工大学学报,2009(01):63-66. |
| [8] | 郝德生;赵家林;刘立佳 等.粉煤灰矿物聚合物的研制[J].齐齐哈尔大学学报,2005,21(03):2-27. |
| [9] | 周文献,谢友均,刘宝举.赤泥对粉煤灰激发作用的试验研究[J].混凝土,2002(01):37-40. |
| [10] | 李珍,韩炜,邵晓妹.地质聚合物在材料领域的应用及其发展方向[J].长江科学院院报,2008(04):93-96. |
| [11] | 孙道胜,王爱国,胡普华.地质聚合物的研究与应用发展前景[J].材料导报,2009(07):61-65. |
| [12] | 汪澜;崔源声.矿物聚合物水泥与混凝土的研究(二)[J].商品混凝土,2005(02):50-52. |
| [13] | 李建平,袁桂芳,王坤英,史珂,倪文.地质聚合物的制备及其在尾矿免烧制品中的应用[J].矿产综合利用,2007(02):38-42. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%