利用极化曲线和失重法,研究了H2S、Cl-、温度等因素对Cr13钢在饱和CO2介质中腐蚀行为的影响.试验表明,在50℃、Cl-浓度为50g/L时,随溶液中H2S含量增加,Cr13钢自腐蚀电流密度增大,钢的腐蚀速率上升,腐蚀受阴极浓差极化控制.50℃,H2S浓度为0.06mol/L时,当Cl-浓度低于50g/L时,随着Cl-浓度增加,Crl3钢腐蚀速率上升;当Cl-浓度高于50g/L时,随Cl-浓度增加,Cr13钢的腐蚀速率下降.在H2S浓度为0.06mol/L,Cl-浓度为50 g/L时,随温度升高,Cr13钢腐蚀速率增加.
参考文献
| [1] | R. Cabrera-Sierra;I. Garcia;E. Sosa;T. Oropeza;I. Gonzalez .Electrochemical behavior of carbon steel in alkaline sour environments measured by electrochemical impedance spectroscopy[J].Electrochimica Acta,2000(4):487-497. |
| [2] | 张忠铧,孙中渠,黄子阳,郭金宝.经济型抗CO2腐蚀油套管用低合金钢的研究[J].宝钢技术,2002(04):37-40. |
| [3] | 张忠铧,黄子阳,孙元宁,蔡海燕,郭金宝.3Cr抗CO2和H2S腐蚀系列油套管开发[J].宝钢技术,2006(03):5-8,59. |
| [4] | 吕祥鸿,赵国仙,杨延清,马志军,陈长风,路民旭.13Cr钢高温高压CO2腐蚀电化学特性研究[J].材料工程,2004(10):16-20. |
| [5] | Dmitry Sidorin;Derek Fletcher;Bill Hedges .The electrochemistry of 13% chromium stainless steel in oilfield brines[J].Electrochimica Acta,2005(20):4109-4116. |
| [6] | S.L. Wu;Z.D. Cui;G.X. Zhao;M.L. Yan;S.L. Zhu;X.J. Yang .EIS study of the surface film on the surface of carbon steel from supercritical carbon dioxide corrosion[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2004(1/4):17-25. |
| [7] | 吕祥鸿,许文研.模拟油田环境中P110钢的CO2腐蚀行为[J].材料科学与工程学报,2008(04):535-539,500. |
| [8] | 李国敏,刘烈伟,郑家燊.碳钢在含硫化氢及高压二氧化碳饱和的NaCl溶液中的腐蚀行为[J].中国腐蚀与防护学报,2000(04):204-210. |
| [9] | 张雷,国大鹏,路民旭.Cl-含量对J55钢CO2腐蚀行为的影响[J].中国腐蚀与防护学报,2009(01):64-68. |
| [10] | 白真权,李鹤林,刘道新,王献昉.模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J].材料保护,2003(04):32-34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%